Electronics Forum | Fri Jun 02 08:50:47 EDT 2006 | russ
Hmmm interesting, we utilize 5 mil stencils and print to same height as you and do not experience these failures. May I ask what paste you are using and what the spacings are of your pad design? But anyhow, if it works it works.
Electronics Forum | Sun Jun 04 21:05:56 EDT 2006 | ec
Hi Russ, I could not send any attach file using smtnet.......anyway thanks your input.
Electronics Forum | Mon Jun 05 07:27:45 EDT 2006 | dwelch123
I have one of these and what I usually do is undersize your measurements just a hair. Also , if you are still using the 3500 vision unit you might want to upgrade to the lantern system. Hope this helps.
Electronics Forum | Mon Jun 05 11:42:17 EDT 2006 | smitty
A discussion started this morning an whether we need to add an N2 line to the reflow oven when we switch over to a lead free process. We will be using OA flux. Any thoughts?
Electronics Forum | Thu Jun 08 09:58:59 EDT 2006 | slthomas
"...and it's definitely humour - Dave what are you doing to our beautiful language???" No worries, Rob. It's being suggested that our use of it is only temporary. ;)
Electronics Forum | Tue Jun 27 09:25:55 EDT 2006 | aj
How does SN100C perform using Selective Pallets? We switched over to SACX about 5 weeks ago and the results are brilliant. We are getting better results than before believe it or not. Also dross foramtion is a lot less. aj...
Electronics Forum | Thu Jun 08 16:46:07 EDT 2006 | proy
I would like to use a no clean paste on an assembly, but seams most no cleans only get to SIR values of 10 E10 or so. Can anybody recommend something with a higher SIR residue? Peter
Electronics Forum | Tue Jun 13 17:46:36 EDT 2006 | jbrower
What???? Look here buddy, What are you a Phd in? I have a few thoughts but I'de like to hear it from you. Just an observation, IF you posted solutions or other useful information you MIGHT get a better response. Jay
Electronics Forum | Fri Jun 09 21:53:07 EDT 2006 | Professor Besserwisser Dr Dr PhD
I am sorry, but I hope No hard feelings? :) As for an answer to Your question: No I can not see the reason for using three heat zones on the wave. Anybody else?
Electronics Forum | Sun Jun 18 04:08:32 EDT 2006 | anilw2006
I am looking for fuji fcp6 machine .but my worry is i can use cp6 for glue procrss? Regards, Anil Wagh.