Electronics Forum | Tue Jan 17 12:25:56 EST 2006 | Cmiller
Pete C, this forum has no value if people do not share thier real world experience. We can all do research on our own. We can all make bad decisions or good decisions based on that research because most of the data we have access to comes from the pe
Electronics Forum | Wed Nov 04 11:35:01 EST 2009 | dilogic
1. can you load cut tape onto the feeders, or only reels? You can, but you have to use cover tape extender (pretty cheap, though) >2. how about parts on trays (like Atmel AVRs in the QFP package)? You need tray feeder. But you can "make" your own
Electronics Forum | Wed Dec 08 11:26:04 EST 2010 | davef
3 Printer Area Conditions * As stated earlier, heat and humidity are damaging to solder paste. Ideally, the printing area should be maintained at 40% - 50% relative humidity and 72°- 80°F (22-26°C). In addition, no air (cool or warm) should blow dire
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Sat Jul 17 13:25:02 EDT 1999 | Scott
| | | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | | | What is it you're tr
Electronics Forum | Fri Oct 16 17:01:21 EDT 1998 | Justin Medernach
| | | | | | It seems like most people want to X-Ray their BGAs. We're going to start doing a lot more of them and need to consider X-ray, too. | | | | | | Q: Do most people/companies X-ray everyBGA or do they just do SPC? | | | | | | Q: Can you get
Electronics Forum | Sat Jul 03 19:24:25 EDT 1999 | JohnW
50% reduction in time. One draw back, the availability of feeders... You need 280 feeders max to change over a max capacity of 140 feeder machine (or a variance of a product mix vs. part numbers); then there's 8mm, 12mm, 16mm, sticks feeders that c
Electronics Forum | Thu Oct 15 14:33:37 EDT 1998 | Earl Moon
| | | It seems like most people want to X-Ray their BGAs. We're going to start doing a lot more of them and need to consider X-ray, too. | | | Q: Do most people/companies X-ray everyBGA or do they just do SPC? | | | Q: Can you get away with spending
Electronics Forum | Thu Oct 15 17:20:25 EDT 1998 | Justin Medernach
| | | | It seems like most people want to X-Ray their BGAs. We're going to start doing a lot more of them and need to consider X-ray, too. | | | | Q: Do most people/companies X-ray everyBGA or do they just do SPC? | | | | Q: Can you get away with sp