Electronics Forum | Tue May 02 13:32:53 EDT 2006 | marvindamaniac
We are using a Metal Screen. We used a metal screen in the past and found that stencil life wasn't a problem. We are a Low Volume, High mix spot where the average lot size is no more than 100 pcbs and as low as 5 pcbs. I am concerned with wiping i
Electronics Forum | Mon May 15 11:25:10 EDT 2006 | muse95
Since when is Hakko putting more plating on their tips? I was told that there was no change to their tips, it was the same tip for Pb or Pbfree. Prior to first use, all Hakko tips are Pbfree. We have been seeing those tips degrade quicker with Pbf
Electronics Forum | Tue May 09 02:18:45 EDT 2006 | Helmi
Hi, My company is using HEPA filter to improve air quality coming out of oven/wave solder. But the cost of such filter is quite high and we need to improve the consumption. Any suggestion from fellow experts out there? a. Anybody did a cost reduc
Electronics Forum | Thu May 11 01:14:29 EDT 2006 | pavel_murtishev
Good morning, There are two ways to solve your problem: 1. Use already written software. For instance, Valor BOM manager has BOM comparison function together with powerful postprocessor and many others. In my opinion, Valor BOM manager is the best t
Electronics Forum | Fri May 12 13:56:37 EDT 2006 | timnop
Steve, Thank you very much for your reply. What I really need to know now is how you discovered these issues. Did you run this product in your wave solder machine, and for how long? Are you now using SN100c instead? Please mention the other issues if
Electronics Forum | Mon May 15 11:16:10 EDT 2006 | timnop
In an attempt to re-establish this thread as a serious request for professional experience and opinions on the Kester K100LD product, let me ask again!..... Have any of you professionals out there tried this product and if so, what was your experienc
Electronics Forum | Mon May 15 17:38:11 EDT 2006 | jbrower
Howdy, I have an Electrovert econopak smt II. I'm set to change over in June to SN100C. I won't be changing out anything. I'll just be purging the lead out of the solder pot with a tin bath. I don't expect there to be any problems with our change
Electronics Forum | Thu May 18 21:05:58 EDT 2006 | Wizard of Oz Tin Man
"Solder alloy compositions are numerous but the most important are still the tin lead solders which were used by the Romans. Tin melts at around 232�C and lead at about 327�C in the combination 62Sn 38Pb the resulting alloy melts at 183�C. This compo
Electronics Forum | Tue May 23 09:55:47 EDT 2006 | TMC
Do you have an automated line with pick and place equipment that can handle your BGA's? Inspecting the board is a must after profile development. You may send the 1st board to a CEM for X-ray inspection. If you have a consistent process (printin
Electronics Forum | Fri May 26 16:24:45 EDT 2006 | Jak
Due to spacing issue, we are considering using power bricks with tin/lead solder ball instead of PTH package. The solder ball is 40 mil diameter. Our CM suggested they do hand place since the pick and place nozzle cannot pick up and hold the part due
We are a global electronics manufacturing Solutions provider ....Our company supplies new and used SMT equipment, spare parts, consumibles, ESD supplies and services to a wide range of EMS companies.