Electronics Forum | Fri Jul 25 15:54:22 EDT 2008 | pcbbuilders
I am trying to optimize my reflow profile. i have a 5 zone oven. lead-free: for the 1st 3 zones, i am good, at about 150-200 deg for 150 seconds. during the 4th zone, i am at a temp of 200-220 for 50 seconds. during the 5th zone, i am at 220-245 f
Electronics Forum | Thu Sep 05 23:18:03 EDT 2013 | feiyangniao
There is a new toy I received today: a NeoDen TM-240A automatic desktop pick and place machine! I’ve kept my eyes on this baby for a quite a while, and finally decided to make a purchase last week. The shipping was very fast: DHL from China, a total
Electronics Forum | Tue Feb 19 16:19:26 EST 2008 | edatasys
Check out http://www.solderstar.co.uk/wavePro.html This tool measures all key wave solder information with a single pass. Wave/PCB contact, immersion depths, etc. Also has a reflow pack to allow use on reflow, 9 channels with predictive software. B
Electronics Forum | Tue Jul 11 10:13:22 EDT 2006 | SWAG
Over time, you might see problems with delam., blistering and warpage if using FR4 carriers. Depending on volumes, you might consider using durostone or some robust material like that for the production runs. Keep in mind that switching materials w
Electronics Forum | Mon Dec 18 23:24:50 EST 2006 | grantp
Hi, Yes, I would hate to resort to cleaning, but the product must be clean. We have been using palettes to keep most of the flux off the PCB, but there is still residue around the connectors. Does anyone suggest a good no clean flux to use with le
Electronics Forum | Fri Dec 15 18:36:46 EST 2006 | Grant
Hi, I have noticed we are getting residue on our wave pcb's and it's worse with lead free, since we changed to the flux we are using. We are currently using Avantec VOC Free flux model Ecofree 303. It looks like it's made in Malaysia. Does anyone h
Electronics Forum | Tue Feb 19 09:41:26 EST 2008 | slthomas
ECD sells the MOLE, and they sell both the Oven Rider and the Wave Rider to accompany it. The thing is, you can profile both an oven and a wave machine without either if you're willing to just solder your thermocouples to a board. The nice thing ab
Electronics Forum | Wed Mar 12 23:00:10 EDT 2008 | davef
You can say: The pad was lifted after reflow and prior to the dye and pry failure analysis. When we see lifted pads, we think: * That's a good solder connection * Either it took a lot of force to lift that pad or the fabrication of the board in the
Electronics Forum | Mon Jul 12 11:35:27 EDT 2004 | Pierre RICHARD
Here are some answers to my questions after a good research. I also added more definitions that could help understand this esoteric language used in assembly, specially surrounding fluxes and their use. In blue italics are comments and extracts from
Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee
If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC
Products, services, training, and consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep & Sole Agent in North America for Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830