Electronics Forum | Fri May 27 10:34:05 EDT 2005 | Rob
Hi Joris, I've used 10's of Millions of these (and the AVX version - PBRC****) and never found this problem (I also worked for Murata back in the mists of time & never encountered it). Internally the part is thermally symmetrical, so the only thing
Electronics Forum | Mon Mar 13 15:35:56 EST 2006 | russ
You're a piece of work! Why don't you work for any of the major wave companies? So how does slowing the conveyor speed eliminate drying flux? And when you slow it down, what speeds it up to make you say "I lower the wave because I get shorts going
Electronics Forum | Tue Jul 11 17:25:31 EDT 2006 | flipit
Moon man was guy who contributed often to smtnet. He had a lot of experience behind him. He breathed nitrogen, drank flux with an occasional shot of 111 trichloroethane, and his lunch consisted of dump bucket vision rejects. He was originally crea
Electronics Forum | Thu Jul 05 22:56:53 EDT 2007 | gyverlo
Hello Sirs: Recently we are having an issue with environmental stress (high humidity or moisture), so we decide to apply conformal coating on our motherboard to protect via holes. According to IPC-A-610D, spec of thickness for type AR is 0.03~0.13 m
Electronics Forum | Sat Aug 18 11:23:10 EDT 2007 | Learn From U
Hi All, Via X-rays, we found solder voids appear on PTH location, especially on Dimm connectors area. We think this should be related to PCB issue as we found solder unable to fill up the PTH hole during bare board testing at wave soldering machi
Electronics Forum | Wed Apr 16 19:23:52 EDT 2008 | molos21
I think you are close to the problem when you expect the pcb having a problem. When I look at your different pics I saw that your via holes looks like this pcb has a hasl finish... and when i look at Q 14 this picture tells me that the pcb is not an
Electronics Forum | Fri Jun 20 03:47:24 EDT 2008 | philip
Hi all, any good recommendation for PbF paste application to reduce voids underneath the QFN thermal pad (stencil thickenss? opening? via hole? reflow profile etc)? We have tried few stencil opening design but no significant improvement as seen. Ther
Electronics Forum | Fri Aug 15 00:51:30 EDT 2008 | boardhouse
Hi Paul, My discloser, I sell for an offshore house, this is Crap.... Section 3.4.3 Annular Ring (External) of IPC-6012A, which also calls out Table 3-5, states that "Plated-through holes identified as vias can have up to 90 degrees breakout of t
Electronics Forum | Fri Aug 22 14:24:54 EDT 2008 | boardhouse
Paul, I would do two things, eval whole lot for any etching issues as shown above and scrap and two I would have your copper thickness checked, my guess your copper plating will be low. Check plating thickness in Via holes - if less then 8/10th's r
Electronics Forum | Fri Nov 14 17:21:17 EST 2008 | cisridn
Plugging the holes with temporary solder mask helped some, but once the solder starts to reflow, the fumes from the flux pushed the solder mask out. What I ended up doing in addition to using the temporary solder mask was covering the areas of pcb w