Electronics Forum | Tue Jan 13 13:42:45 EST 2004 | Tom Parkinson
We use a MIRTEC high res bench top system and are real happy with the performace. We have used it for both pre-reflow Mainly checking parts and part numbers) and post reflow for everything including solder joints. Easy to program and as you do more
Electronics Forum | Tue Jan 13 02:43:48 EST 2004 | Bryan
Hello all, As everyone knows,for all kinds of reasons we must change the reflow oven from 8 zone to 12 zone,but how?perhaps the easiest way is to buy a new 12 zone oven...however what will you do then with the old 8 zone oven,scrape? is there anyone
Electronics Forum | Tue Jan 13 21:00:15 EST 2004 | davef
This sounds like something the saleman of your new Vitronics oven should be happy to help you sort through. ECD [and probably other profiler supplers] provide software for playing with [optimizing?] recipes. In it, they allow you to select from a v
Electronics Forum | Tue Jan 13 04:35:26 EST 2004 | pablowe
We have done some trials with Lead free which appear to have gone well. We will be introducing a number of new products over the coming months and it is an opportune time to begin using lead free on these products which will be required by law in the
Electronics Forum | Tue Jan 13 20:52:21 EST 2004 | davef
Bismuth Solder alloys * Fatigue life is reduced when soldered to hot air solder leveled (HASL) boards. * Lead from Hot Air Leveling (HAL) coatings can diffuse through the grain boundaries of alloy. * Lead is bismuth alloys can form a eutectic composi
Electronics Forum | Fri Jan 16 15:31:26 EST 2004 | davef
Bill This drives solder suppliers nuts, because it's not analytic: Dross inclusion testing can be conducted on the base solder in the solder pot and the virgin solder. Conduct this test by heating a sample of solder, contained in a clear beaker,
Electronics Forum | Tue Jan 13 16:40:03 EST 2004 | Jacob Lacourse
Hi folks, I have a conformal coating application where I need the coating to be UV stable for a number of years without any crazing or cracking of the coating. I have looked for such a coating and have come up empty handed. Much of the circuit boar
Electronics Forum | Tue Jan 13 18:03:38 EST 2004 | Ron
I believe Megellen Service would do this for you. I see another company has decided to replace Contact before they go under. I know some people do not believe Contact will go under but believe me when I tell you they only have months left. Apex will
Electronics Forum | Thu Jan 15 09:40:47 EST 2004 | davef
Search the fine SMTnet Archives. For instance: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=24429 Do not get your hopes up about finding something to support your "leaching out of silver theory", though. * AgxSn IMC are disbursed ro
Electronics Forum | Fri Jan 16 14:24:11 EST 2004 | dwoodrow
We would like to start testing our lead free wave solder machines in house. Mostly looking for lead and copper content. Malcom makes a relatively inexpensive machine that does this (STA-1 http://www.malcomtech.com/products_sta1.html). Does anyone