Electronics Forum | Mon Aug 23 20:21:00 EDT 2021 | jorgealvarado
does anyone know what equipment I can use to test high current EV batteries? We want to expand our testing capabilities and standardize all our battery testing. Looking for feedback from anyone who has used test equipment for electric vehicle batteri
Electronics Forum | Tue Aug 24 20:24:30 EDT 2021 | cbeneat
We have X5's. You are able to turn inspection on/off on the screen. Obviously an older machine running XP. I have never had a bad experience with ASYS support. I usually call our regional Field service rep. Where are you located?
Electronics Forum | Fri Sep 03 07:33:46 EDT 2021 | sophyluo1985
Sorry, sir, I don't want to disturb you, or have other thoughts. I know you will not trust Chinese people now, but we want you to know that not all Chinese suppliers are like this. You can try to contact GOLDLAND, there will be no loss for you, maybe
Electronics Forum | Sat Oct 23 08:16:32 EDT 2021 | smtconnie
Sorry to hear your story. We are professional SMT line machine manufacturer in GuangDong China.(ICT International Group). We provide oversea service for many country clients. We have many agent in different country. We also put advertisement in thi
Electronics Forum | Tue Sep 14 04:16:55 EDT 2021 | mokshamanthra
Thanks DWL, we have a board with double sided SMT components now. and there is an intrusive component on the bottom side which is build first. the connector pin is extending out by 0.3mm and this is causing printing issues when building top side. we
Electronics Forum | Wed Sep 08 04:10:14 EDT 2021 | leeg
Thanks Davef, we are using a mill max pogo pin on a small pcb that is panelised into a panel of 50, we have had a jig designed to get them straight instead of hand placing, there are 4 per pcb. We have followed the manufacturers guidance for stencil
Electronics Forum | Wed Sep 08 07:54:32 EDT 2021 | majdi4
So wetting was unstable and slow . You need to do a wettability test to make sure about that defect .Also a material analysis to know the composition of the materials that constitute the components . if you get negative test results , you need to do
Electronics Forum | Sat Oct 16 03:04:21 EDT 2021 | jessicasu
> Slanting Issues after reflow if u are using <BR> > thru-hole type, u might need to define the <BR> > slanting degree allowed during prototype. =) <BR> <BR> there is adding the insulating plastic will sol
Electronics Forum | Fri Sep 10 15:15:09 EDT 2021 | majdi4
Hello to all , Could you help with this defect .. Tombstoning 0201 , always at the same place in board , only this component near to the coax connector..with a defect rate of 2 % ..All the process is perfect . i cheked : stencil design , SPI resul
Electronics Forum | Mon Sep 13 07:27:50 EDT 2021 | denism
There may also be a problem with the a thermoprofile. Measure the temperature of both contacts of the component, if they heat up not evenly and the soldered lead heats up faster, then the problem is in the profile. To solve the problem of misalignmen