Electronics Forum | Fri Sep 26 09:47:34 EDT 2008 | kevslatvin
I hope this doesn't add any confusion. I save my data as a .csv file and bring that into Cad2cad. This is how I was shown to do it by Assembleon. To use .csv you have to set your file format on the format cad file tab(during import to Cad2cad) to Cha
Electronics Forum | Sat Nov 29 09:56:59 EST 2008 | blacksi27
What the other user was talking about is correct, converting it from gerber to machine cad. It is hard explaining programming SMT to a new user unless shown by another experience operator. I am also getting a topaz x pretty soon and I'll try to hel
Electronics Forum | Fri Sep 19 21:31:15 EDT 2008 | trynders
Thanks for the response guys! The parts are being sent to a local lab as we speak. I'll let you know the results when I get them. I am not sure the purpose of the copper band, but the black around the band is just shadowing from how I took the pi
Electronics Forum | Fri Sep 19 10:20:20 EDT 2008 | mi
I asked the stencil house we go to for quote on 29"x29" & anything larger stencil. Your board size converts to just 16.22"x26.9685". I don't know the next stencil size after 20"x20". Maybe, common is 29"x29"? I also asked about "frameless" stencils
Electronics Forum | Fri Sep 19 10:24:10 EDT 2008 | jtownsend
I am looking to replace our current smt line of a Contact 3S. This has been our only machine and we have had it for about 6 years. We are looking for 100 plus feeder capacity and 10k plus placement rate with a diverse component range. I am considerin
Electronics Forum | Mon Sep 22 11:55:26 EDT 2008 | wrongway
you might want to check out panasonic they can handle a lot of feeders on one machine and are fast We have universal advantis machines have had them for a year have'nt had any problems yet. have not had universal calibrate them yet still placing par
Electronics Forum | Mon Sep 22 15:32:20 EDT 2008 | davef
We see this fairly often. It doesn't affect solderability. Our analysis makes us think this coloration is copper. The reason copper appears on the surface may be that heat cycles increase the thinness and porosity of the immersion silver [IAg] coatin
Electronics Forum | Mon Sep 22 15:25:37 EDT 2008 | davef
Most of the BIG suppliers of uV materials also offer ovens. Equipment, Assembly, Adhesive, Curing System, uV 1 Integrated Dispensing Solutions, 5311 Derry Ave Building D, Agoura Hills CA 91301; 818-597-4300 F818-597-4301 http://www.dispensinglink.co
Electronics Forum | Mon Sep 29 17:15:26 EDT 2008 | gdzuber
Hello, In a membrane generator there are almost no moving parts. So, the maintenance would be to replace the active carbon filter, and seals, about every 2~3 years. Normal life should be 10+ years. To prevent problems, the compressor must be oil-fre
Electronics Forum | Tue Sep 23 13:08:26 EDT 2008 | slthomas
Put the new stuff in the back and pull from the front. A pass through from stores makes that a lot easier. Bar codes are a wonderful thing if you can get people to use them. Wand it into stores then wand it sequentially into production via a queue.