Electronics Forum | Tue Jun 20 07:26:45 EDT 2017 | emeto
Thank you for the detailed input. That gave me material to think on.
Electronics Forum | Mon Jun 19 07:59:01 EDT 2017 | emeto
Hello, I am planning to use a water wash flux. As this is new to me, would you guys share what should I be aware of? I know cleaning PCBs itself presents issues. If you can share your experience so I can prepare better, it would be great.
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl
Electronics Forum | Fri Feb 04 09:23:21 EST 2000 | Casimir Budzinski
If No-Clean flux does not need to be cleaned, then why do I get readings of up to 27(ug NaCl/sq in) on boards that are not washed, up to 23.4(ug NaCl/sq in) on boards washed with DI water only and from 1.2 to 10.1(ug NaCl/sq in) on boards washed with
Electronics Forum | Thu Sep 26 11:44:23 EDT 2002 | abelardo
Hello everyone out there in the SMT world. I have a dilema I'm currently running a board that has 3 csp's with a .75 mm. ball pitch and .3mm ball size. And 2 qfp's-160. The stencil is 4 mils thick and I'm using a 63/37 solder paste. My reflow prof
Electronics Forum | Thu Sep 26 20:43:51 EDT 2002 | davef
"OK. If the connection doesn't look like I expect it to look, how do I know that the metallurgy is correct?" Comments are: * There are no pictures that will get you though this. * You should expect that gold that is dissolved in Pb/Sn solder to make
Electronics Forum | Tue Aug 30 12:08:09 EDT 2005 | slthomas
The answer for us at my previous employer was water soluble flux. Wash the board, no residue. If you're not set up to wash (needing a washer, DI water source, waste treatment, ventilation, etc.) it can be expensive and space consuming. Do some resea
Electronics Forum | Tue Aug 30 10:46:27 EDT 2005 | lyrtech
Hi, I curently have an interesting challenge. But I don't have all the knowledge to solve it. One of our boards is used in RF applications. We noticed that the No-Clean flux residue makes interferences in the RF signal. Removing the flux residue so
Electronics Forum | Tue Aug 30 15:05:23 EDT 2005 | Shean Dalton
Dear Ing, Have you analyzed why some RF device aren't operational after washing? An assumption is that failures are related to the ultrasonic energy applied. Other possibilities are for poor rinsing, poor drying, inadequate washing on those failed
Electronics Forum | Sat Feb 05 09:08:18 EST 2000 | Dave F
Casimir: Let me expand on something that I said in my response to your thread on ionic testing. Generally, no-clean people don�t use ROSE testing as part of their process control, because the ROSE test is essentially washing your board in DI/IPA �