Electronics Forum | Sun Nov 08 15:27:25 EST 2015 | davef
Thinner: Flux thinner, NOT paint thinner We kept a spare stone in thinner in inventory. We cut PVC pipe to size, cap in one end, screw thread on the other, stone inside, filled with flux thinner and covered with a screw cap. I don't remember who we
Electronics Forum | Sun Apr 25 12:05:50 EDT 1999 | Chrys Shea
| | | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free solderin
Electronics Forum | Mon Apr 26 09:18:27 EDT 1999 | C.K.
| | | | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free so
Electronics Forum | Thu Jun 22 10:33:03 EDT 2017 | charliedci
We are changing /adding a lead free wave. This will either be a conversion of a leaded wave or a new purchase. Nitrogen seems to be a necessity in selective soldering lead free, should I presume the same for a wave process? I am interested in first h
Electronics Forum | Thu Apr 15 11:13:24 EDT 2004 | pjc
Sn corrosion effects were studied for stainless steels, coated stainless steels, titanium, cast iron, and other materials. This study can be found in the SMT Library under "Equipment Impacts of Lead-Free Soldering" Electrovert uses a Melonite coating
Electronics Forum | Tue Apr 24 16:06:33 EDT 2007 | coop
I was just wondering if anybody has noticed a greenish/muddy color to their solder. It is just a very thin layer that can be easily be skimmed away but comes back shortly, I was just wondering if this an indication of a contaminated solder pot, we ha
Electronics Forum | Thu Sep 08 08:54:09 EDT 2005 | Slaine
if the problem is wetting change the flux type. have you tried adjusting the temperature of the wave? if your getting 100% wetting id decrease the wave temperature, or try a flux that is less active.
Electronics Forum | Tue Aug 31 21:45:49 EDT 2004 | KEN
I have experienced this directly in SMT and wave solder. Fillet lift (can) be a direct indicator to lead enrichment (but its not the exclusive symptom). Lead enrichment in smt joints reduces the interfacial strength shortening the time to creep f
Electronics Forum | Thu Oct 13 15:41:30 EDT 2005 | lyrtech
Hi, We have a customer who give us a 20K board contract each year. It's only thru-hole components.The baord is HASL plated. So we pass it into our wave. No problems. Recently, our customer decided to go into GOLD PLATED finish. We take the same re
Electronics Forum | Thu Jul 23 16:49:04 EDT 1998 | Ted
I was wondering how successful industry has been in quantifying relationships between defects rates of particular solder problems (like bridging, opens,..) and PCA design parameters (like spacing, part orientation, pad dimensions, ...). For wave sol