Electronics Forum | Thu Jul 09 21:17:18 EDT 1998 | Dave F
According to Howard, we clean the flux tank on our wave solder machines every week. We replace it because flux sops up moisture from the air and contaminating materials from boards that are being fluxed prior to soldering. How would a prudent perso
Electronics Forum | Sat Nov 04 22:26:33 EST 2000 | Aoki Laboratories Ltd.
Greg, The operating parameters for Wave Soldering are: 1. Preheat Temp. (80-110 c, board surface); 2. 1.5-3 secs dwell time in solder. This, 1.5 second, is the time required for both the lead and solder to gain sufficient heat and as a result "tinn
Electronics Forum | Mon Apr 21 09:28:06 EDT 2003 | Bryan
What does acrinym---BNY mean? can't you use Paste In Hole process,if the pitch is large enough?You can find imformation about PIH everywhere. we have tried PIH,selective soldering,wave soldering,and found that wave soldering get the best solder joint
Electronics Forum | Sat Mar 12 18:32:29 EST 2011 | jlawson
It is pretty hard to wave solder fine pitch parts bad enought with 0.5mm let alone 0.4mm It can be done but need N2 inert wave soldering & need layout design to accommodate this... Iy it is a QFP need to run part 45 deg into wave and if possible in
Electronics Forum | Fri May 21 11:20:42 EDT 2004 | Cal
We actually use a solective soldering fixture for our wave soldering process. cal
Electronics Forum | Sun Apr 03 00:18:47 EST 2005 | Haran
What is the minimum pitch for PTH component not tend to have solder shorts during wave soldering process.
Electronics Forum | Tue May 22 08:39:23 EDT 2012 | davef
Bridging Causes: Insufficient flux, excessive pre-heat, high conveyor speed, solder contamination [AIM Solder]
Electronics Forum | Fri Jun 01 10:43:43 EDT 2012 | signal
Perhaps apply the through hole part, solder mask only one barrel. Then hand solder that single leg.
Electronics Forum | Fri Dec 14 10:59:23 EST 2001 | Donald C. Burr
We are considering converting from a water wash wave solder porcess of carbon ink touch pad buttons to a no-clean process. Since the carbon ink buttons are exposed to the molten solder, we are concerned about the residue that is left behind from the
Electronics Forum | Tue Mar 15 08:02:36 EDT 2011 | davef
Yes, you can reflow solder SMT parts with pads designed for wave soldering [including 1206] providing that you design your stencil apertures properly. It's a momma, poppa, baby bear situation. * Wave solder sized apertures will put too much paste on