Electronics Forum | Thu Jun 22 09:50:48 EDT 2017 | capse
Are you using nitrogen in your soldering process?
Electronics Forum | Tue Jun 20 15:08:30 EDT 2017 | ranap121212
Hello I have the problem with selective soldering on the robot. Thin balls appear on the laminate. The tin sometimes shoots...? and then the balls are a few millimeters from the soldering point. I tried up or down with temperature, but it did not wor
Electronics Forum | Wed Mar 01 16:59:44 EST 2000 | Dave F
Robert: Expect a 0.033" raw ball to be within 0.022" of the pad, after reflow. To be clear, that�s not a matter of shrinking by 33%. The volume of solder on the pad is the same as the volume of solder in the raw ball. It�s just that the solder is
Electronics Forum | Wed Mar 01 16:59:44 EST 2000 | Dave F
Robert: Expect a 0.033" raw ball to be within 0.022" of the pad, after reflow. To be clear, that�s not a matter of shrinking by 33%. The volume of solder on the pad is the same as the volume of solder in the raw ball. It�s just that the solder is
Electronics Forum | Mon Jun 26 08:57:17 EDT 2017 | capse
If N2 is not an option, the cut wire feeder or drilled wire are your best bet for now. You need to optimize wire feed rate as well. The solder joint on the robot takes about the same time to form as in manual soldering. If you need to speed the solde
Electronics Forum | Thu Jun 22 15:05:55 EDT 2017 | solderingpro
There are several different technologies in the industry today to assist in the out-gassing of flux cores. On automated soldering systems, there are two main types of perforating solder feeders: - Hole Drilling - "V" Scoring By perforating the so
Electronics Forum | Wed Jun 21 19:01:48 EDT 2017 | mac5
Try baking the boards; you may have a moisture problem.
Electronics Forum | Sat Jun 24 07:49:58 EDT 2017 | ranap121212
@Capse, No but the machine has such a construction, I can not this change
Electronics Forum | Fri Feb 19 14:43:46 EST 1999 | Nithy
We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not be
Electronics Forum | Thu Jun 27 21:28:42 EDT 2002 | davef
You're correct that the Ni/Pd termination seems to have something to do with you solder balling. It could be related to the interaction between your paste and the Pd. I assume these are really 'fines' rather than 'balls'. Things that come to mind a