Electronics Forum | Mon Mar 13 06:11:08 EST 2006 | Rob
Surely this is a job for Wavemaster Larry? Have you tried flux buster pins in your ICT yet? They are quite good at cutting through the crap on a board.
Electronics Forum | Mon Mar 13 12:53:21 EST 2006 | slthomas
"Surely this is a job for Wavemaster Larry?" I know this is supposed to be a serious forum, but that's some funny stuff! 8 mil stencils. Suuuuure.
Electronics Forum | Wed Dec 24 20:29:45 EST 2008 | xianhua_tang
Oh,I consider the process is wrong,it is stencil print paste-mount-reflow -apply glue-reflow,then wave solder. it must pass twice reflow,also the first reflow profile is different and the second .
Electronics Forum | Tue Jan 10 14:44:42 EST 2006 | greg york
Not sure about Sn/Cu/Ni large market share here in Europe as we have a large part of the UK market with SACP0307 alloy 0.3%Ag introduced over Two years ago Also worked against Sn/Cu/Ni alloy with large TV Co and they went with 0.3%Ag due to reliabili
Electronics Forum | Wed Feb 02 21:17:55 EST 2000 | Steve Harshbarger
Istvan, The advise from both Roni and Mike sounds right on the money. The problem is most likely that your PCB is not completely dry (the flux has not completely evaporated) in the area where these solder balls occur. You have a number of differen
Electronics Forum | Mon Sep 28 10:12:53 EDT 1998 | Chrys
| Hello, | I need some users information about "Air knif" in wave soldering: | 1. Does it decreases bridging ? | 2. Is it self installed of a purchesed kit (if purchesed, who are the recomended vendors) ? | 3. Any other information about the issue. |
Electronics Forum | Mon Jan 15 09:19:29 EST 2007 | tk380514
We use Alpha EF-2202 low-VOC No-Clean flux Selective wave soldering cassettes Bottom pre-heating wave soldering machine We have one component that will not solder properly: http://www.epcos.com/web/generator/Web/Sections/ProductCatalog/Capacitors/Ul
Electronics Forum | Mon Mar 13 15:35:56 EST 2006 | russ
You're a piece of work! Why don't you work for any of the major wave companies? So how does slowing the conveyor speed eliminate drying flux? And when you slow it down, what speeds it up to make you say "I lower the wave because I get shorts going
Electronics Forum | Thu Aug 28 16:03:08 EDT 2008 | wavemasterlarry
I guess you're adding the gas to keep the fingers clean - sounds likeyou got your threads mixed up on the Forum. Any way I would suggest not doing this. Gas is pretty flammable. I have pix of one our Hollis cleaning machines going up in flames cau
Electronics Forum | Fri Mar 31 12:27:27 EST 2006 | Marcus
We have used the SN100C for over a year now with fanastic results. We use the SAC305 for SMT and SN100C wire exclusively. There are no problem mixing the alloys. I am also on the commitee for the NASA testing. The SN100C did out perform SAC and SnPb