Electronics Forum | Wed Oct 23 14:45:00 EDT 2002 | Tom G
I haven't tried anything like that but had some experience with .8 mm pitch SSOPs. Immersion depth in wave was very critical- had to control Lambda pump speeds within 20 RPM and even then it would change as solder level dropped. Need thieving pads o
Electronics Forum | Wed Sep 15 11:05:16 EDT 2004 | rlackey
Hi John, It depends on what equipment and resources you have at your disposal - if you have an antique wave with crap adjustment & hand sprayed flux, no debridging/air knife system on a tightly packed board with a multitude of fine pitch connectors
Electronics Forum | Wed Nov 01 08:55:05 EST 2006 | russ
See if the solder is leaving the pad(s) and is wicking up the component. This is long shot but I have seen something similar to this possibly in a wave process. We had a very thin board and a very large QFP on top. During wave operation the solder
Electronics Forum | Mon Feb 19 11:14:49 EST 2007 | realchunks
WaveRiders do work well. But they just measure, do they do not adjust anything. It's up to you or your staff to interpret and adjust your machine accordingly. It�s one of those tools that is affective, but only to the extent of you�re willing to u
Electronics Forum | Mon Jun 14 10:23:53 EDT 2010 | pcrane
I have CCA that has a SN100C HASL coating that I am wave soldering with SbPb. I have mounting pad areas on the CCA that are masked with a pallet during reflow so they are not exposed to the solder. The mounting pads are turning gray in some areas of
Electronics Forum | Tue Dec 07 04:23:27 EST 2010 | Jacki
Dear All I hope I can get some advice of PCB experts in here.My problem is - after wave, our big board, 640x420x1.7mm, had a warpage when the board was cooled down after wave. PCB was flat while being warm.I had tried with many type of pallet and mad
Electronics Forum | Wed Oct 15 23:41:34 EDT 2014 | padawanlinuxero
Hello Chris I had a similar problem, what work for us was a combination of fluxer and preheat, we try different approaches what work was high pressure and a low traverse speed, and really heating up the upper part of the board, you see we need to u
Electronics Forum | Thu Jun 17 22:10:48 EDT 1999 | Earl Moon
| | | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | | | for example: | | | | | | Solder Bridge | | | 1.verify amount of flux been aplied. | | | 2.verify turbulance on
Electronics Forum | Mon Jun 14 13:47:54 EDT 1999 | Chrys Shea
| We are a medium sized PCB assy. house manufacturing about 2000 motherboards a day. There is a major problem we are facing at the wave soldering stage, i.e. warpage of the PCB. As soon as the PCB touches the wave it warps severely from the centre
Electronics Forum | Wed Jun 16 07:34:17 EDT 1999 | Glynn Technologies and Manufacturing
| | We are a medium sized PCB assy. house manufacturing about 2000 motherboards a day. There is a major problem we are facing at the wave soldering stage, i.e. warpage of the PCB. As soon as the PCB touches the wave it warps severely from the centr