Electronics Forum | Mon Sep 09 10:50:24 EDT 2002 | bmulcahy
Hi MK, It not really as simple as changing from one to the other. VIA hole, PTH hole sizes may need to be changed. Really the designer should re-evalaute the board before changing. Also remember your soldering profiles, both reflow and wave (if appl
Electronics Forum | Fri Dec 01 06:41:54 EST 2006 | CHITRA K
We get both leaded components and lead free ( MIX OF COMPONENTS) components . In order to achieve good soldering results, please provide generic profile for reflow and wave soldering .
Electronics Forum | Thu Sep 15 07:03:38 EDT 2011 | mosborne1
This looks like a flux problem to me. I would check the specific gravity of the flux. Also check the thermal profile of th e wave solder process.
Electronics Forum | Mon May 14 09:24:36 EDT 2001 | rkevin
Can anyone shed some light on this for me ? Subject: Soldering to Immersion Tin surface finish I am looking for info. (pro and con) and/or 1st hand knowledge processing PCB's with Immersion Tin finish through SMT and Wave. Do profiles need to be di
Electronics Forum | Wed May 12 10:21:37 EDT 2004 | solderpro
having a bad morning there Gregory.... take it easy, where you from? who's company? Do you rep this firm or is this yours? I surely did not mean to disrepect your input, but I am sure there are things you need to learn that are not in the operators m
Electronics Forum | Fri May 07 16:24:08 EDT 2004 | bruce @ knoll
I did have my solder analyzed and it is clean. The Hollis preheat coils are a bit hard to control but I have measured the board top side and I am getting a temp of 105c just before wave contact. I would like to move to a spray fluxer but I am going
Electronics Forum | Fri Jul 29 06:16:19 EDT 2016 | dmsm123
We do have a commen problem with flux residues after the wave soldering process, even after using correct wave soldering profiles recommended by the flux supplier, The following flux type is being used Alpha EF 2210 VOC Fre Bellcore No Clean water Ba
Electronics Forum | Thu Apr 12 03:55:06 EDT 2001 | surachai
Dear anyone ; Every time that we run profile now ,we will create profile from recommendation of vendor flux and the some critical parameters such as thermal shock or others ... but I don't know that Do you ever create standard profile to be procedure
Electronics Forum | Tue Jun 10 16:51:19 EDT 2003 | davef
Develop your recipe wave soldering exactly as you developed your recipe for reflow soldering. The only difference is that instead of using your paste supplier's recommendations as the starting point, use your flux supplier's recommendations as a bas
Electronics Forum | Wed Dec 28 20:56:14 EST 2016 | anhsang38
Dear Pro, Pls, try to get solder's profile from solder supplier. That is the most important in wave soldering process... if not you will be difficult for improvement. Good luck.
.gif)