Electronics Forum | Mon Dec 17 02:08:21 EST 2007 | mun4o
Hi, I have a lot of solder bridge in our wave soldering process.We use SACX0307 and Surf 11 flux.the SW mashine is Vitronics delta 6622.Itry to change flux and termoprofile but results is not god.Can you halp me - recommend me some flux or other adv
Electronics Forum | Mon Dec 17 12:06:58 EST 2007 | pjc
5 Steps to Eliminate Bridges: 1. Establish (wave) Parallelism First and foremost, you must establish board-to-wave parallelism. This is the prerequisite to any wave solder process control. For an understanding of the power of this approach go to ht
Electronics Forum | Fri Apr 02 02:37:43 EST 2004 | darburch
We are asking $10,500us for this machine, as for shipping I will see what I can come up with as we are in Canada. This is a dual wave machine with foam fluxer. It has not run in 3 years but when we had it in production results were favorable and cons
Electronics Forum | Fri Jan 28 12:18:32 EST 2005 | Chunks
Your best bet is to do a decision making matrix. Each company has so many different criteria�s it's hard to pick out which one might be important to yours. Simply pick out your top 5 paste manufactures. Next decide what your "Eliminators" are - th
Electronics Forum | Thu Nov 17 20:51:16 EST 2005 | cangly
Morning Mike, We use Pb63/Sn37, Alpha Metal alloy. Solder pot is at 250 C. The profile of board after Preheat about 100 C, Lambda Wave about 220C (use both Lambda and Chip wave), DWell time 2.1s ~ 3s. Conveyor speed 1.5 in/min. We run by bare board a
Electronics Forum | Tue Jul 13 14:19:00 EDT 1999 | JohnW
| | | Hi, | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | | | Sec
Electronics Forum | Tue Jul 13 14:25:57 EDT 1999 | Earl Moon
| | | | Hi, | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | |
Electronics Forum | Wed Jul 14 21:34:16 EDT 1999 | karlin
| | | | | Hi, | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | |
Electronics Forum | Thu Jul 15 14:38:38 EDT 1999 | JohnW
| | | | | | Hi, | | | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants)
Electronics Forum | Mon Mar 13 15:35:56 EST 2006 | russ
You're a piece of work! Why don't you work for any of the major wave companies? So how does slowing the conveyor speed eliminate drying flux? And when you slow it down, what speeds it up to make you say "I lower the wave because I get shorts going