Electronics Forum | Tue May 03 07:44:45 EDT 2005 | mmjm_1099
Try this: http://www.smtnet.com/forums/index.cfm
Electronics Forum | Tue May 03 04:59:33 EDT 2005 | jaume
Does anyone has experience with this soldering process? I would appreciate to have some information, about equipment and procedures Many thanks
Electronics Forum | Tue Mar 10 04:36:41 EDT 2015 | vb7007
Hi I have been struggling with boards for high quality picky customer. I am getting flux waves (like splashed - too hard to clean) after wave, where as we are still using Kester 979 (No clean flux, but as we are getting visible marks which looks si
Electronics Forum | Tue Mar 10 04:37:32 EDT 2015 | vb7007
Hi I have been struggling with boards for high quality picky customer. I am getting flux waves (like splashed - too hard to clean) after wave, where as we are still using Kester 979 (No clean flux, but as we are getting visible marks which looks si
Electronics Forum | Fri Jul 07 14:11:14 EDT 2006 | japsola
I have noticed the Chinese wave solder manufacturer's are using chillers for their nitrogen inerted waves. I am perplexed as to why they do this as I haven't seen this on any other manufacturer's equipment manufactured in North America. Any ideas wh
Electronics Forum | Fri Jun 12 23:52:42 EDT 2015 | armandogomez
Reflow? or Wave solder? or selective wave solder? For what I understand you problems is with the preheaters you have a high temp that dries up the flux, and when hits the wave is doing that, do you have a thermal profiler? what's the temp just befor
Electronics Forum | Thu Jul 20 16:14:59 EDT 2000 | Cole
How effective will current wave solder equipment and processes be with lead free solder? What temperatures will be required? How will dross generation compare?
Electronics Forum | Wed Mar 28 14:11:19 EDT 2007 | pjc
It should only be a visual thing. What may be happening is that all the thermal energy being driven into the wave solder pallet to get good soldering is causing the no-clean residues to burn up a bit, causing the discoloring. Check to see if they hav
Electronics Forum | Fri Jun 12 11:15:50 EDT 1998 | Ryan Jennens
Hey all! The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pallet w
Electronics Forum | Wed Mar 28 13:14:38 EDT 2007 | amelara98
I am having problems with a product we receive from our overseas plant, where there is excessive "dullness" of solder joints/metal surfaces after running a board on a pallet through wave solder. Seems to be an issue of the pallet, as the solder appe