Electronics Forum | Wed Aug 18 11:25:12 EDT 1999 | J.J. Thomas
| WE ARE CURRENTLY HAVING PROBLEMS REFLOWING BOARDS WITH WHITE TIN PLATING. WE ARE NOT GETTING GOOD WETTING ON THE PADS. | WE HAVE CHECKED THE REFLOW PROFILE AND TRIED DIFFERENT PASTE'S. | WE THINK THERE MAY BE CONTAMINATION OR OXIDATION ON THE PADS.
Electronics Forum | Thu Jun 24 12:43:08 EDT 1999 | Earl Moon
| | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody h
Electronics Forum | Tue May 04 10:38:24 EDT 1999 | Dave F
| Does someone has experience with solder stop on components to avoid an Viking effect (no solder on the pad, all solder on the lead)? What kind of solder stop does work well? What is dangerous? What has to be kept in mind when using such components?
Electronics Forum | Fri Dec 18 00:49:43 EST 1998 | Mr Mariscal
I have been developing a BGA Process and are having problems with a 310 IO PBGA reflowing. I am achieving good wetting exept 2 to 5 balls on the outer perimeter I have a good profile my air flow is set per mfg spec, the strange thing is that it does
Electronics Forum | Fri Dec 18 00:48:35 EST 1998 | Mr Mariscal
I have developing a BGA Process and having problems with 310 IO PBGA reflowing. I am achieving good wetting exept 2 to 5 balls on the outer perimeter I have a good profile my air flow is set per mfg spec, the stange thing is that it does not happ
Electronics Forum | Wed Oct 28 15:34:45 EST 1998 | carlm
| Can anyone supply me with info on determining the volume of paste left on a pad once reflowed compared to the intial amount put down? Is there a formula or something? | That information should be contained in the technical data sheets supplied by
Electronics Forum | Sun Jul 05 12:47:44 EDT 1998 | Bruce Carnegie
What should a good gold joint look like? We've run boards for our customers that look kinda dull but seemed to wet properly and the boards fired up just nicely! Should they look nice and shiny like our HASL boards or is "a shiny joint is a good joint
Electronics Forum | Tue May 19 05:42:36 EDT 1998 | Earl Moon
| Earl, | I admit that I missed your article since I seemed to have let my subscription to Circuit Fabrication Magazine expire. I am interested in your experience in this area. Is there a way to get a copy of your paper? Could you maybe post it to
Electronics Forum | Thu Apr 16 08:07:05 EDT 1998 | Stan
Currently I am in the buisness of soldering bare die to the top surface of a copper heat sink. Is any one else have some exprience in this process that can help. We heat a copper slug through a contolled atmosphere, place a preform then a bare die.
Electronics Forum | Mon Mar 30 03:10:44 EST 1998 | Patrick Ng
Hi, We have encountered de-wetting issues with gold plated components( SMT LEDs ). The problem comes and go and we yet to locate the root cause ( process, component or solder paste etc ). The rest of the components on the boards are not having this