Electronics Forum | Wed Oct 06 11:40:41 EDT 1999 | Debbie Alavezos
| | Hi, | | | | Help! Could anyone help to enlighten me on this? | | | | Question: | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowable Y/Z or X/Z that using a n
Electronics Forum | Fri Jun 08 08:26:14 EDT 2007 | davef
Testing for solder mask cure: Search the fine SMTnet Archives, for instance: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=15726 Residue after wave: Water in your wave soldering flux may cause your NC flux residue to go white. Indium W
Electronics Forum | Wed Oct 06 00:26:04 EDT 1999 | Karlin
| Hi, | | Help! Could anyone help to enlighten me on this? | | Question: | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowable Y/Z or X/Z that using a normal water cl
Electronics Forum | Thu Feb 12 12:30:16 EST 2015 | stevezeva
I remembered something from the TechNet a long time ago about heating the board with a heat gun to see if the white spots disappear. I searched the archives and found this from Bill Kenyon: Quick identification of solder mask white spots- if it is t
Electronics Forum | Thu Jul 15 18:50:43 EDT 1999 | Raeto Zryd
We intend to use VOC free fluxe in our nytro machine. Does anybody know if there can be problems with water ie. solvent residues in the tunnel. Perhaps there are some white papers available on that issue.
Electronics Forum | Fri Jan 19 06:49:34 EST 2001 | Adam
To you wavesoldering guru's. When wavesoldering with a selective wavesoldering carrier What causes the white vapor type residues around the areas of the carrier which are exposed to the wave ? My Initial reaction was to high of A Pressure for the spr
Electronics Forum | Wed Jul 21 17:49:52 EDT 2004 | jsk
problem: Too many solvents and boards are not clean Flux remains on the board after vapor degreaser and "Powdery" white residue after vapor degreasing Flux type is kester 186 Process: hand solder High Temp alloy, spot clean after hand solder e
Electronics Forum | Fri May 29 17:48:34 EDT 1998 | Earl Moon
| | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localize
Electronics Forum | Sat May 30 08:24:09 EDT 1998 | Dave F
| | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not locali
Electronics Forum | Sat May 30 12:51:29 EDT 1998 | Earl Moon
| | | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not loca