Electronics Forum | Mon May 07 11:02:17 EDT 2001 | Singh
Hi all. I am looking into the implementation of the Chip on Board process with eutactic bonding and the then using either gold or aluminum wire to make wedge type wire bonding. Since I am totally new to this, can somebody guide me thru the process,
Electronics Forum | Mon May 07 22:29:52 EDT 2001 | davef
4 wire per sec ... you figure how many you need] Encapsulation ~$120K for a dispenser [10 sec per die ... you figure how many you need] plus a cure oven ~$100k Throw in a another ~$100k for marking and cleaning Check the September 2000 SMTnet New
Electronics Forum | Mon May 07 15:13:03 EDT 2001 | jdtpfacreate
Singh, The equipment varies in price. We make a wire bonder called the HW27U-H Wire Bonder. This is a gold to gold wire ball bonder. The substrate size you mention is within the area we can take into the machine. The key is the bonding area.
Electronics Forum | Tue Jun 04 19:33:16 EDT 2002 | rob_thomas
Dave's estimation is pretty conservative but there is a lot of equipment out there and a lot of people happy to make a sale.Implementing both mentioned processes it's difficult and time consuming .Even if you get good training from whoever sells you
Electronics Forum | Mon Jun 03 12:51:17 EDT 2002 | V.RAMANAND KINI
We are doing COB operations for nearly ten years. Pls. write to me if you need info on m/c selection, type of PCB, plating etc., Thanks V.RAMANAND KINI...03.06.02
Electronics Forum | Tue Oct 07 12:35:10 EDT 2008 | andy_pal
Hi All, I am using COB on my DOUBLE SIDED PCB. lastly we used Eletrolytic Ni / Flash Gold Plating. Our Boards vias Failed the UL corrosion Test. we did some cross-section analysis and found 10.75 �m of Nickel and 0.022 um of Gold and as the Process
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Fri Aug 28 23:32:39 EDT 1998 | Pete Sorenson
| Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? | What are the limitations? | Thanks, | Steve I have used silver epoxy extensively for conductive bonding applic
Electronics Forum | Wed Jan 09 21:19:49 EST 2002 | davef
When I said "In this area, there is no difference between your experience in ceramic substrates and PTFE substrates." I was referring to the area we were discussing ... gold plating. I am sorry if you thought I ment than the wire bonding process wa