Electronics Forum | Wed Nov 09 11:01:41 EST 2005 | DannyJ
Hi Red and Greg, First, to Avalancher, the service that is mentioned is fantastic. I have used it various times with various connectors and headers with fantastic results. Just contact MyData and they'll tell you what they need. It's usually 5-1
Electronics Forum | Sun Nov 27 11:32:30 EST 2005 | cyber_wolf
They may tell you it will solder lead free,(and it may) but trust me...you are going to have nothing but headaches. If you start flooring the heaters you are going to put it into a "melt down" after a while. I know you don't want to hear it, but tak
Electronics Forum | Sat Dec 03 16:26:40 EST 2005 | grantp
Hi, I have seen demos of these scopes, and don't think they really show you very much. If you profile your board right, and drill up to solder a thermocouple onto the inner balls of the device so you really know your getting a good profile, I don't
Electronics Forum | Wed Dec 14 12:48:21 EST 2005 | grantp
Hi, A second hand TP9-2U MYDATA could be picked up very low cost, however it will only load a single component at a time, which could be ok for your jobs. However if your running 0402, I am not sure if that model will do it accurately. Your machin
Electronics Forum | Thu Dec 22 10:51:12 EST 2005 | killer1994
Yes, I have been using it for 4 years now. We have the 4 axis, 3 head, 2 lines. Inspection station and ir oven. I have to say you will NOT get better support anywhere in this industry than from PVA. Their crew is top notch, always going above and bey
Electronics Forum | Sat Dec 17 15:46:28 EST 2005 | Csabee
Samsung SM320 don't have sensor for recognizing component. Only using Fly&Fix camera. In first time the korean samsung service engineer advised me (3,7light settings for chips and the machine generated many dumps, sometimes 50 or more per day. But n
Electronics Forum | Mon Dec 19 08:56:18 EST 2005 | davef
Q1a. If the thickness of the silver is too much (how is too much??), A1a. We have heard stories of using Ag2 to limit silver [or gold] dissolution, but have never seen formal studies to demonstrate that idea. First, exclude the use of silver plate
Electronics Forum | Wed Dec 21 12:19:58 EST 2005 | DannyJ
Hi Mark, We're not doing anything too fancy. We have a couple of programs that do assist us, but in all reality, they are mainly front-ends for a database. The first is a program called Global Shops that we use for our inventory. This is based o
Electronics Forum | Thu Dec 22 08:57:08 EST 2005 | davef
Immersion metal baths also rely on alchemy-like magic. If you take a piece of copper and dip it into an aqueous solution of silver ions: Presto Chango! Within seconds the copper will be coated with silver. Of course, there is some additional magic re
Electronics Forum | Thu Dec 22 12:05:37 EST 2005 | Tony
Currently we are using a 2 step vapor soldering process to manufacture our std. lead soldered parts. The first step was done with a ls240 vapor fluid and the second was done with a ls200 fluid. Using a 221 deg C sn95/Ag5 solder for the first step a