Electronics Forum | Mon May 10 15:49:52 EDT 1999 | Steve Gregory
| | Can anyone tell me what the recommended "typical" cooling rates are after reflow? Are the cooling rates considered as critical to control as the heating rates and why/why not? | | I do not think there is a "typical" post reflow cooling rate out
Electronics Forum | Fri May 07 08:06:03 EDT 1999 | Hon Choi
| | Hi all, | | | | We're starting up tests for pin-to-paste and, well, things could be better. We're testing different pastes and we're testing different apertures rules and, well, we're still testing. It's coming close and we're getting pretty
Electronics Forum | Sun Apr 25 12:24:45 EDT 1999 | Chrys Shea
| Hello all, | | Our guys here still have some questions on the "optimized" profile which sees a more moderate ramp up straight to reflow temperatures versus the conventional profile which has a plateau at around 150 Celsius. If the optimized profi
Electronics Forum | Sun Apr 25 14:43:34 EDT 1999 | Earl Moon
| | Hello all, | | | | Our guys here still have some questions on the "optimized" profile which sees a more moderate ramp up straight to reflow temperatures versus the conventional profile which has a plateau at around 150 Celsius. If the optimized
Electronics Forum | Mon Apr 26 12:51:45 EDT 1999 | Bob
Steve, Moisture sensitivity needs to be taken seriously. Being in the commercial end of electronics now, I am using many plastic packages. Unfortunately, moisture sensitivity processing is not black and white and it does require procedures and dis
Electronics Forum | Fri Mar 19 07:24:38 EST 1999 | John
| | | | Hi folks, | | | | | | | | I am looking for inputs on a long-standing problem encountered in our shop: Bottom-side parts (passives) falling off in the Wave...where the only remnants of the part is a flattened glue dot of proper diameter and
Electronics Forum | Wed Jan 06 21:17:31 EST 1999 | Dave F
| Hey All you Einsteins out there!! | | I gotta' problem...('course you do Steve, or you wouldn't be bugging the TechNet now would you?) I had a phone call from a acquaintance of mine wanting to bring two prototype boards over to rework a BGA socket
Electronics Forum | Tue Dec 08 17:55:51 EST 1998 | Dave F
1. What is the best way to remove polyurethane conformal coating from selected areas? Your conformal coat material supplier is best equipped to tell you how to remove the coating. Polyurethane conformal coating is not easy to remove. Without in-pu
Electronics Forum | Wed Oct 14 15:33:48 EDT 1998 | Justin Medernach
| | | | | We suffered our first blood letting because of razor sharp edge clamps (DEK 265LT) and operator giving it the finger. While positioning magnetic tooling pins, one of our best slipped and really sliced off a part of his main digit. This will
Electronics Forum | Mon Sep 14 07:49:37 EDT 1998 | Earl Moon
| | Thanks for the help, Guys. | | As a matter of interest, I'm going to look up the standard and see if there's a European (or preferably UK) equivalent. If I find anything, I'll post another Follow Up (though I doubt it holds much interest for you)