Electronics Forum | Thu Aug 16 10:59:08 EDT 2007 | mika
Did You recieve any s/w with it? If something has happend to the hard drive or something could happens in the future then you need to reinstall... S/W ver. is written on the the s/w package. It should contain s/w for: The OS (Operating system), Visi
Electronics Forum | Fri Aug 17 15:59:02 EDT 2007 | mika
A quick guide... But let me tell you the essentials in the beginning/middle of next week (I will then copy "our way"). There are 3 consecutive steps of how to proceed. Maybe I can e-mail you this in a word doc, where I can put in screen shots? I don'
Electronics Forum | Wed Aug 22 09:53:06 EDT 2007 | slthomas
"The question is: should we be looking at the operator? the paste? or the setup?" Yes. ;) Those guys love to brag about their 4 corner height adjustment on those printers. The fact is it's a PITA and shouldn't be necessary in the first place. It's
Electronics Forum | Fri Aug 24 14:15:24 EDT 2007 | clarkk
Ben, I'm not aware of any 'automatic' method to convert PTH footprints to SMT. Typically, many of the components are passives, and there may be a way in your CAD software to change the passives of a common size to a different footprint. That will co
Electronics Forum | Thu Aug 30 11:02:51 EDT 2007 | gmoritz
... talking two-lead LEDS with 2.5mm pitch ... Yes. That's what we are working with. > are the LED terminals shape were Square or > the naturally rounded? Some are round. Some are square. One is U-shaped. > Due to different insert rotations,
Electronics Forum | Wed Sep 12 17:09:11 EDT 2007 | allwave
HI John, I use wave fixtures with titanium inserts. So far I have not seen any problem with walls about 0.010" thickness and 0.120" tall (or deep depending how you see it)...The Titanium-composite interface is also very strong (as long as you have e
Electronics Forum | Thu Sep 27 17:25:33 EDT 2007 | chef
The short answer is immediately after reflow the problem occurs. To be more exact, what you are describing is not "rust". Rust occurs in iron. The oxidation that occurs in Tin-Lead has been sometimes called "white rust". Either way, oxidation occur
Electronics Forum | Fri Oct 12 10:16:37 EDT 2007 | stepheniii
How do you measure how pregnant a woman is? A component is ROHS compliant or it is not. If a component is not compliant and is put into an otherwise compliant assembly then that assembly is no longer compliant. I doubt anyone on here does any calcula
Electronics Forum | Fri Oct 12 14:13:30 EDT 2007 | stepheniii
If I need a lawyer I'll look you up. To get into that kind of detail you will have to look at the legislation itself in question. And I"m sure if there were any such loophole it would be plugged by now. But we had a customer that found something l
Electronics Forum | Fri Oct 19 10:49:48 EDT 2007 | brulal1
Hi I will like to know what do you think about cleaning hand solder, my employee spend about 25% of they time to brush they hand solder with teddy pen cleaner, we used no clean solder wire. It�s not been the first time that I try to eliminate those c