Electronics Forum | Fri Mar 26 17:12:43 EDT 2010 | spitkis2
Krish, Looks like your peak temperature is around 230C and time above 183C is about 120-150 seconds. This is excessive for a leaded BGA. You should be aiming at 200 - 215C as the peak joint temperature with time above 183C of 60 -90 seconds. The p
Electronics Forum | Thu Apr 08 13:28:24 EDT 2010 | mabdalla
Thanks DucHoang, One more favor. Will really appreciate if you can point us on how to figure out the number of patterns (number of offsets) from the VIOS file. Also we would like to know the feeder types represented by the numbers in the &F sectio
Electronics Forum | Fri Apr 02 14:11:21 EDT 2010 | bigdaddysoy9
Manjunath, I prefer orthogonal systems. In my experience they are actually better at detecting coplanarity and HIP defects than multi camera systems. They are obviously limited, in that they can not inspect a component under another component, b
Electronics Forum | Fri Apr 09 09:08:40 EDT 2010 | cast2010
Hello, I produce two types of board. - 100% Thru Hole - 50% thru hole and 50% SMT For the second, I have a bad wetting after the reflow on the top. The pcb board have Au-Ni pad. I use a water soluble paste. I clean the board with a solution with
Electronics Forum | Fri Apr 09 15:00:04 EDT 2010 | davef
So for your SMT1/SMT2/PTH boards, you have poor solderability during SMT2. [Even if you have no SMT2 and only ST1/PTH, our answer is the same.] We assume this occurs on one board part number only. We guess that your bare boards have insufficient gol
Electronics Forum | Sun May 02 11:36:27 EDT 2010 | jdeluna
I do agree with Jerry: you should apply more paste on it, either with a step stencil, or doing overprint on it by, let's say 120% on Transformer's pad. Also, you need to check : a) there's smooth movement on transport process after the placement, no
Electronics Forum | Mon May 03 11:20:43 EDT 2010 | mikesewell
A good guideline is keep it similar to your wave solder process, for example 2-3 sec. This assumes you're preheating the assembly. While polyimide boards are fairly robust at some point you will begin to see copper dissolution - the solder side pad
Electronics Forum | Wed May 12 17:54:22 EDT 2010 | jlawson
Just a note, on fixed galden machines yes the way they compensate for rise time is as the previous post suggested, change power and also stage the lowering of the PCB into the vapor cushion ie not the main one but further up in the tank. The disadvan
Electronics Forum | Fri May 28 01:47:05 EDT 2010 | jeffr
I have the part you need. The Yamaha Part number is K39-M7173-000. The same part is used on Philips machines using a different part number. This assembly is expensive because the motor is attached to a Harmonic Gearbox and encoder. I have a new unit