Electronics Forum | Wed Oct 10 07:01:05 EDT 2007 | jdumont
I agree, I have been doing this for years also. Never found anything that the oven wasn't already telling me. I will however be investing in the KIC 24/7 constant monitoring device soon. Price isn't too bad for what you get. Customers like to get a w
Electronics Forum | Fri Oct 12 15:52:41 EDT 2007 | etienne
Hope that your PCB is supported evenly, I mean really plane to the conveyer rail. If not this may warp the PCB upwards, causing fiducials to be identified not accurately. Also I suggest you to check Mark Info of the fiducials and have a look at the t
Electronics Forum | Thu Oct 18 14:30:37 EDT 2007 | wayne123
I talked to someone regarding the Biral oil and they said that they have had a problem with it "jelling up" when exposed to oxegen. Has this been a problem for you as well? I ordered some Stabylyn 773ND from Vitronics. I hope this stuff works for 57.
Electronics Forum | Fri Oct 19 13:04:14 EDT 2007 | brulal1
Thank Rob those are our own product, try few test by not clean some PCB never had any issue except on compoment under faraday cage. Did you know any norm that could persuade my boss and the R&D department that cleanning no clean is a waste of time. T
Electronics Forum | Fri Oct 19 13:57:17 EDT 2007 | Michael Konrad
Hi Rob, I must take issue with your statement �By definition, no clean solder can be not-cleaned�. All no-clean fluxes can be cleaned. Whether or not one cleans no-clean depends on a variety of factors. More than eighty percent of all post reflow
Electronics Forum | Mon Oct 22 21:34:36 EDT 2007 | davef
Double check on this, but we have this little voice in our heads telling us that your AgPd termination is intended for conductive adhesive applications. Check with your component supplier. We recall a thread on SMTnet [ http://www.smtnet.com/forums
Electronics Forum | Mon Oct 29 15:31:02 EDT 2007 | mulder0990
How long ago was this? I can't find anything under 7K. It is 17K for the Fuji all in one, the only one they sell. I am not even looking into the GAM20. The feeder master is the one that I am considering. If you find a better deal, I would be hap
Electronics Forum | Fri Nov 02 12:51:29 EDT 2007 | adtech
Is your data scewed in any fashion? If not the board is fine. If the cosmetics are an issue, write a procedure to have them changed out based on the criteria you choose (testing results, cosmetics etc.). This will be essential if your company is ISO
Electronics Forum | Sun Oct 28 08:32:47 EDT 2007 | davef
With a 7 thou stencil, we'd go 1 to 1. So for a more typical 6 thou stencil, we'd bump the aperture area by 1.15, maybe 1.2. We make no distinctions between 'innies' and 'outies'. Are you talking about castellations on land grid devices [ie, BCC�, L
Electronics Forum | Thu Oct 25 21:33:24 EDT 2007 | hussman
Castellated is the easiest lead design. Anything longer than the out side dimension of the part should be OK. However, you will never get an inspection person to say it looks OK, yet the solder joint occurs on the bottom side of the part - like a B