Fatigue Damage Behavior of a Surface-mount Electronic Package Under Different Cyclic Applied Loads.

Published:

July 10, 2014

Author:

Ren Huai-Hui, Wang Xi-Shu

Abstract:

This paper studies and compares the effects of pull–pull and 3-point bending cyclic loadings on the mechanical fatigue damage behaviors of a solder joint in a surface-mount electronic package.

The comparisons are based on experimental investigations using scanning electron microscopy (SEM) in-situ technology and nonlinear finite element modeling, respectively. The compared results indicate that there are different threshold levels of plastic strain for the initial damage of solder joints under two cyclic applied loads; meanwhile, fatigue crack initiation occurs at different locations, and the accumulation of equivalent plastic strain determines the trend and direction of fatigue crack propagation. In addition, simulation results of the fatigue damage process of solder joints considering a constitutive model of damage initiation criteria for ductile materials and damage evolution based on accumulating inelastic hysteresis energy are identical to the experimental results. The actual fatigue life of the solder joint is almost the same and demonstrates that the FE modeling used in this study can provide an accurate prediction of solder joint fatigue failure....

  • Download Fatigue Damage Behavior of a Surface-mount Electronic Package Under Different Cyclic Applied Loads. article
  • To read this article you need to have Adobe PDF installed

You must be a registered user to talk back to us.

 

Company Information:

A research university located in Beijing, China, and one of the nine members in the C9 League.

Beijing, China

Research Institute / Laboratory / School

  • Phone +86 10 6279 3001

See Company Website »

Company Postings:

(1) technical library article

  • Jan 17, 2023 - Introducing Closed-loop Nitrogen Control To Solder Reflow | Heller Industries Inc.
  • Jan 17, 2023 - How Challenging Conventional Wisdom Can Optimize Solder Reflow | Heller Industries Inc.
  • Jan 17, 2023 - The User Benefits of a Supplier Partnership | Heller Industries Inc.
  • Jan 17, 2023 - Vacuum Fluxless Reflow Technology for Fine Pitch First Level Interconnect Bumping Applications | Heller Industries Inc.
  • Jan 17, 2023 - Flux Management | Heller Industries Inc.
  • Browse Technical Library »

Fatigue Damage Behavior of a Surface-mount Electronic Package Under Different Cyclic Applied Loads. article has been viewed 537 times

  • SMTnet
  • »
  • Technical Library
  • »
  • Fatigue Damage Behavior of a Surface-mount Electronic Package Under Different Cyclic Applied Loads.
SMT feeders

One stop service for all SMT and PCB needs