Intermetallic Growth in Tin-Rich Solders
Published: |
June 13, 2017 |
Author: |
Louis Zakraysek |
Abstract: |
For tin-rich solder alloys, 200 C (392 F) is an extreme temperature. Intermetallic growth in tin-copper systems is known to occur and is believed to bear a direct relationship to failure mechanisms. This study of morphological changes with time at elevated temperatures was made to determine growth rates of tin-copper intermetallics. Preferred growth directions, rates of thickening, and notable changes in morphology were observed. Each of four tin-base alloys was flowed on copper and exposed to temperatures between 100 C and 200 C for time periods of up to 32 days. Metallographic sections were taken and the intermetallics were examined. Intermetallic layer thickening is characterized by several distinct stages. The initial growth of side plates is extremely rapid and exaggerated. This is followed by retrogression (spheroidization) of the elongated peaks and by general thick-... |
You must be a registered user to talk back to us. |
Company Information:
More articles from General Electric »
- Jan 30, 2019 - Novel Pogo-Pin Socket Design for Automated Low Signal Linearity Testing of CT Detector Sensor
- See all SMT / PCB technical articles from General Electric »
More SMT / PCB assembly technical articles »
- Mar 19, 2024 - What is Underfill | GPD Global
- Mar 19, 2024 - Made in Japan: Solder Paste Jet Dispensing Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 26, 2024 - Precision Control in Electronic Assembly: Selective Wave Soldering Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 02, 2024 - Maximizing Efficiency: The High-Speed SMT Line With Laser Depanelizer | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Dec 27, 2023 - Revolutionizing Tech: SMT Auto IC Programming Machine Mastery | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Browse Technical Library »
Intermetallic Growth in Tin-Rich Solders article has been viewed 1065 times