Controlling Moisture in Printed Circuit Boards
Published: |
May 1, 2019 |
Author: |
Bhanu Sood, Michael Pecht |
Abstract: |
Moisture can accelerate various failure mechanisms in printed circuit board assemblies. Moisture can be initially present in the epoxy glass prepreg, absorbed during the wet processes in printed circuit board manufacturing, or diffuse into the printed circuit board during storage. Moisture can reside in the resin, resin/glass interfaces, and micro-cracks or voids due to defects. Higher reflow temperatures associated with lead-free processing increase the vapor pressure, which can lead to higher amounts of moisture uptake compared to eutectic tin-lead reflow processes. In addition to cohesive or adhesive failures within the printed circuit board that lead to cracking and delamination, moisture can also lead to the creation of low impedance paths due to metal migration, interfacial degradation resulting in conductive filament formation, and changes in dimensional stability. Studies have shown that moisture can also reduce the glass-transition temperature and increase the dielectric constant, leading to a reduction in circuit switching speeds and an increase in propagation delay times. This paper provides an overview of printed circuit board fabrication, followed by a brief discussion of moisture diffusion processes, governing models, and dependent variables. We then present guidelines for printed circuit board handling and storage during various stages of production and fabrication so as to mitigate moisture-induced failures.... |
You must be a registered user to talk back to us. |
Company Information:
More articles from CALCE Center for Advanced Life Cycle Engineering »
- Dec 05, 2022 - No-fault-found and intermittent failures in electronic products
- Oct 31, 2022 - Microstructure and Intermetallic Formation in SnAgCu BGA Components Attached With SnPb Solder Under Isothermal Aging
- Jan 26, 2022 - Adhesion and Puncture Strength of Polyurethane Coating Used to Mitigate Tin Whisker Growth
- Dec 21, 2021 - Using Simulation to Optimize Microvia Placement and Materials to Avoid Failure During Reflow
- Dec 16, 2021 - Reliability Evaluation of One-Pass and Two-Pass Techniques of Assembly for Package on Packages under Torsion Loads
- See all SMT / PCB technical articles from CALCE Center for Advanced Life Cycle Engineering »
More SMT / PCB assembly technical articles »
- Mar 19, 2024 - What is Underfill | GPD Global
- Mar 19, 2024 - Made in Japan: Solder Paste Jet Dispensing Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 26, 2024 - Precision Control in Electronic Assembly: Selective Wave Soldering Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 02, 2024 - Maximizing Efficiency: The High-Speed SMT Line With Laser Depanelizer | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Dec 27, 2023 - Revolutionizing Tech: SMT Auto IC Programming Machine Mastery | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Browse Technical Library »
Controlling Moisture in Printed Circuit Boards article has been viewed 1065 times