Electronics Forum | Tue Apr 08 12:16:58 EDT 2008 | pstone
I have four IP3�s all that require different height board support pins. Is there a way to adjust the table height so all of the machines are the same?
Electronics Forum | Tue May 22 12:47:52 EDT 2007 | cyber_wolf
Is there anyone out there using this ? It looks like they only sell it for the 643 machines. Can it be adapted for 642 machines as well ? We have 2 major problems: 1. Operator makes width change adjust without removing supports from previous job. Ta
Electronics Forum | Thu Apr 10 12:28:49 EDT 2008 | cyber_wolf
Why not post the solution for all to see ? Answer: A-cuz then I can't spam.
Electronics Forum | Thu Apr 10 17:35:25 EDT 2008 | fujillews
if you need help just ask
Electronics Forum | Thu Apr 10 18:00:14 EDT 2008 | tonysmt
Thanks llew explanation & information was a great help.
Electronics Forum | Wed Apr 09 13:30:16 EDT 2008 | fujillews
Hi, Please email me directly at llew@alternativesmt.com i will explain how and provide the information you require. Regards Llew
Electronics Forum | Thu Apr 15 12:40:22 EDT 2004 | Claude_Couture
How about graphite coated wires or bar? If there are such things
Electronics Forum | Thu Apr 15 11:13:24 EDT 2004 | pjc
Sn corrosion effects were studied for stainless steels, coated stainless steels, titanium, cast iron, and other materials. This study can be found in the SMT Library under "Equipment Impacts of Lead-Free Soldering" Electrovert uses a Melonite coating
Electronics Forum | Thu Apr 15 10:58:16 EDT 2004 | mwg9184
I am trying to put a center support on a wave solder machine for lead free soldering. My problem is that every metal I use is interacting with the lead-free metals and thus eating away the center support. I have tried titanium, stainless steel. I am
Electronics Forum | Thu Apr 15 20:55:36 EDT 2004 | Ken
Try: Tungsten, tungsten carbide, ceramics like boron-nitride or how about pyrex glass? Glass blowers could make "hooks" that connect to a cross bar. I would NOT use aluminum (even if anodized). Try stainless steel 316. 303, 304 do not have enough