Hi All, after many years of talking about it we WILL be setting up a lead free line. What alloys and products would you recommend. We are seeting up a new wave machine here soon and could us some input.thanks
Electronics Forum | Fri Mar 01 17:39:58 EST 2013 | davef
The LF wave solder solder alloy that marketing-types of other LF wave solder alloys compare themselves to is Nihon Superior SN100C
Electronics Forum | Fri Mar 14 05:38:42 EDT 2008 | meritajs
Hello Could somebody inform us about real consumption of lead free solder alloy SN100C on your wave solder process. We do not use some antiaxidant and had had alloy consumption about 1 kg per hour. What is your experiance? All sugestion will be well
Electronics Forum | Fri Oct 08 08:26:03 EDT 1999 | Carol Zhang
| | | I have a board, 4 spacers needed to be soldered on the board | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, ther
Electronics Forum | Thu Oct 07 16:57:02 EDT 1999 | Glenn Robertson
| | I have a board, 4 spacers needed to be soldered on the board | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there wi
Electronics Forum | Fri Oct 08 10:08:48 EDT 1999 | Glenn Robertson
| | | | I have a board, 4 spacers needed to be soldered on the board | | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first,
Electronics Forum | Thu Mar 20 09:01:33 EDT 2008 | meritajs
Thanks Greg Our main problem is that we are putting small number PCB through, about300 PCB, size180*250. Such number order our customer in week. In result we got such high solder consumption and high production cost. We will tray to use antiacidant.
Electronics Forum | Fri Mar 21 08:39:38 EDT 2008 | lococost
If you are saying you're going through 1kg/h while only producing 300 pcbs a week and the rest of the time the machine is standing still, then 1.there is something seriously wrong with your machine or 2. check if an operator is suddenly covered in sh
Electronics Forum | Tue Mar 18 05:32:09 EDT 2008 | gregoryyork
What volume of boards are you putting through. 1Kg per hour does sound very high but then again it does depend on volume Using an antioxidant is a must with Lead Free some alloys have additions in them to start with but those drop out with use so th
Electronics Forum | Thu Mar 11 01:54:55 EST 1999 | Marcus Reichenberger
Hello everyone, at the Institute for Manufacturing Automation and Production Systems of the University of Erlangen (Germany) one focus of our research activities is the use of lead-free solder alloys for electronics production. In different publicat