Electronics Forum | Mon Aug 27 11:51:47 EDT 2012 | cobham1
Its no my turn to give some advise. My first question would be can you put the boards into a carrier of some sort. There are many wonderful companies that make carriers that are ment for running down a smt line. This can be expensive unless you order
Electronics Forum | Tue May 03 09:47:03 EDT 2005 | denismeloche
We sell rework stations for all kind of components and boards. The systems are designed to fit a particular size board and it's very difficult to design a one size fits all system. I personally have a lot of experience reworking high mass, high hea
Electronics Forum | Tue Sep 27 17:03:07 EDT 2005 | Jay Brower
Hi Steve, When I drain our wave solder pot in preparation for loading a lead free alloy (SN100); I am going to use muffin tins dusted with baby powder or maybe a little high temp oil so that the solder doesnt stick to the tins. I know that this may
Electronics Forum | Fri Apr 04 18:16:43 EDT 2014 | garym4569
We are in the process of launching a new product and found reflow solder issue with one of the inductors. I have set oven profile to paste specifications. I just finished profiling with thermocouple under problem component. All other components ex
Electronics Forum | Fri Apr 18 14:25:51 EDT 2014 | horchak
what is the technology? Is there fine pitch, double sided, number of layers, lead free? If the pcbs are not of the highest quality you may be set up for failure with no clean process. Couple things to look at is your paste flux content versus medal
Electronics Forum | Fri Feb 25 04:28:49 EST 2000 | Sze-Pei LIM
We faced terrible void issue while using Sn96.5Ag3.5 solder paste, more than 20% void. We tried adjusting the reflow oven profiles but we did not have much success in reducing the void. Generally, we find quick preheat, high peak temp. and fast cooli
Electronics Forum | Fri Oct 06 08:48:11 EDT 2000 | CAL
NJEV- You can contact me off line for my opinion on the Easi line :caldon@smtnet.com. Compared to past products this one was weak. Missing parts, Screws sticking out, the thermo-sensor was right next to the button so the longer you held the button th
Electronics Forum | Fri Feb 25 04:28:49 EST 2000 | Sze-Pei LIM
We faced terrible void issue while using Sn96.5Ag3.5 solder paste, more than 20% void. We tried adjusting the reflow oven profiles but we did not have much success in reducing the void. Generally, we find quick preheat, high peak temp. and fast cooli
Electronics Forum | Tue Sep 21 11:01:59 EDT 2004 | pabloquintana
Cleaning method will depend on the type of flux > that you use in your soldering process. Yes it is isopropyl alcohol. We use "no-clean" halide free flux (Multicore X33-06i). We still cleaning and I beleive it is because we roto trim the leads aft
Electronics Forum | Sun Apr 03 03:48:05 EDT 2005 | iwan
I have a problem in my Lead Free smt production line,i run BGA product for the first time. The product consist BGA and Connectors. If i increase temperature in Reflow Oven it will be melting the Connector, but when i decrease the temp. BGA become raw