Electronics Forum | Mon Oct 28 18:59:25 EST 2002 | tkenny007
Specs for Bow and Twist for PCBs (IPC-A-610C, 10.6. There may be an update by now). I also have a note in our quality guide referencing (IPC-TM-650, 2.4.22) and (MIL-STD-105D). In summary, a PCB should not bow more than 0.040" with all four corner
Electronics Forum | Thu Jun 22 11:42:29 EDT 2000 | Chrys Shea
Sal, Silly question: Were the parts skewed before they went into the oven? I've chased down a few similar reflow problems in my lifetime, only to find out it was a pick and place problem. Wrong nozzle size, bad nozzle, feeder not advancing all
Electronics Forum | Mon Dec 10 04:15:01 EST 2001 | Beny
Thanks for your advise Now I don't found Non-wetting defect at TIN COATED 0603 after I had increased peak temp and Time above 183 C. At film caps, I still found Non-wetting in high rate at film chip size 2416. I using PANASONIC's part with identif
Electronics Forum | Mon Aug 16 11:58:29 EDT 2004 | Dreamsniper
I've worked with a Vapor Phase Oven a semi-automatic and a manual oven for evaluation. They worked fine and produce better grain of solder joints. The fluid that you need depends on the solder temperature that you require. I've used a 200'C fluid for
Electronics Forum | Thu Dec 06 23:34:25 EST 2001 | Beny
Pls. help. I�ve problem with non-wetting defect at capacitor termination. I have faced this problem at the 2 kinds of termination. One is chip capacitor 0603 that its outer termination surface composed with 100 Sn (Lead free) and another one is Sta
Electronics Forum | Thu Jul 14 04:28:45 EDT 2005 | lloyd
Folks, Thanks for all the info and suggestions but let me add a bit more to the pot. Our products work in a harsh environment and are classed as safety critical. Customer returns are our biggest concern, we don't get very many and feeling here seem
Electronics Forum | Thu Apr 19 21:49:29 EDT 2001 | davef
SCREENING... 1. Is type 4 paste necessarily required? [No, not unless you are using it for some other purpose.] 2. Is No-Clean Ok to use? [YES] 3. How thin stencil is required? 5 mils? [5 is OK, but I wouldn�t base the decision on the 0201. 6 mil is
Electronics Forum | Sat Dec 04 18:55:38 EST 2004 | Grant
Hi, Yes, all you really need to do is boil the fluid while suspending the PCB above the vapor, so it's quite easy. However I would recommend against dropping the board direct into the vapor cloud, as that would be a very fast warm up, while letting
Electronics Forum | Fri May 11 09:56:58 EDT 2012 | cyber_wolf
Paste control is a subject that has a lot of unfounded claims surrounding it. What is the difference in having a "working paste jar" and a "new paste jar" Either way new and old are getting mixed at some point. We just don't buy onto the whole thing