Electronics Forum | Mon Aug 25 14:55:51 EDT 2008 | grics
I have a question for the manufacturing masters... We are going to start running test trials/DOE of a Urethane Coating (Humiseal 1A33) and I am not sure what to expect. From what I understand, urethane coating is pretty difficult to work. It is supp
Electronics Forum | Tue Aug 26 16:18:13 EDT 2008 | grics
hey, thanks for the advice. We have replaced all the lines and have had the valves cleaned & rebuilt, so we are hoping that will be sufficient. What does the dewetting of the urethane coating look like???
Electronics Forum | Mon Jan 28 11:50:23 EST 2013 | johng
Good morning Mark, No issues around the masking at this point. The issue seem to be in open areas as well as between clad runs. We are using Humiseal 1A33 Conformal Coat.
Electronics Forum | Mon Nov 06 10:51:23 EST 2006 | SteveH
We have 2 PVA2400 4 axis selective spray machines that we use to spray Humiseal 1B31 and 1A33. They take a bit of programming to get right, though this is easy to do, but do the job OK. Another to consider if you need the 4 axis of movement would b
Electronics Forum | Fri Sep 02 16:30:02 EDT 2011 | duso02
Rich That is a standard reaction with Humiseal 1A33, nothing to worry about. Find a board that was coated over year ago and had been heated up at all and it will be an amber color. It does not violate the IPC for discoloration. We have coated boards
Electronics Forum | Tue Feb 03 13:47:59 EST 2009 | grics
I would also suggest looking at your ramp rate in the cure oven. We noticed that accelerated heating increased the "gas out" of the solvent. We run 1A33 and and do not exceed a .5/degC ramp rate.
Electronics Forum | Fri Aug 07 16:45:35 EDT 2020 | duso02
All URs require a long time to fully cure. And actually, most users do not reach full-cure before using the board. Even Humiseal 1A33 will be dry enough to handle after a very short time.
Electronics Forum | Wed Aug 27 08:06:43 EDT 2008 | davef
Thick, hard conformal coatings of acrylic, urethane and epoxy have a well documented history of causing solder joint cracks and breaking glass/ceramic and other brittle components. Dissimilar expansion and fairly high surface bond strengths of the ma
Electronics Forum | Wed Jan 31 10:56:23 EST 2018 | dontfeedphils
I'm working on bringing up a new conformal coat process/workcenter and have a few questions I'm hoping someone might have experience with. Right now we're manually spraying both coating materials (1B31 and 1A33 from Humiseal) using HVLP guns. I run
Electronics Forum | Tue Feb 24 09:47:45 EST 2015 | rgduval
Well, since you're looking at a water soluble flux from AIM, I'm guessing you wash the boards before you conformal coat them. Thus, I wouldn't expect any interaction between the excess flux that you're washing off of the boards and the Humiseal that