Michael: Two things: 1. Profile: A. Your FR4 profile will not produce good solder connections on your ceramic substrate. Hey wait a minute, you soldered FR4 at 250C?? Ceramic is a themal sponge. You'll need to play, but it should be easy compare
Electronics Forum | Fri Nov 13 09:55:08 EST 1998 | Chrys
| We are experiencing 'lifting' on one or more sides of a QFP. Poor lead co-planarity has been ruled out by independent tests. Please tell me which of the two remaining failure modes is the most probrable? | | 1. Expansion of gases in vias underneat
Electronics Forum | Thu Nov 19 05:25:07 EST 1998 | karlin
| | We are experiencing 'lifting' on one or more sides of a QFP. Poor lead co-planarity has been ruled out by independent tests. Please tell me which of the two remaining failure modes is the most probrable? | | | | 1. Expansion of gases in vias und
Electronics Forum | Tue Jan 20 13:33:14 EST 1998 | Justin Medernach
| This is a re-post of my previous message. I typed my Email address wrong in the other message. I am sorry for any inconvenience caused. | Is there anyone who can tell me what is the maximum allowable soldering temperature when soldering a TQFP (Thi
Electronics Forum | Thu Apr 19 20:01:30 EDT 2012 | eadthem
some things to consider, Is there flux on the board. are there finger prints on the tops of parts. Is the board warped at the V score from reflow Is the board shifting in the machine during inspection. These are the issues we have had with our mir
Electronics Forum | Fri Apr 20 14:11:27 EDT 2012 | rway
Programming is different, yes, but so is the terminology. ///with machine vision you have parameters that select what is good and what is bad, and you have parameters that help make bad look worse and good look better making the difference between w
Electronics Forum | Mon Jan 10 18:35:05 EST 2011 | eadthem
Ive used a Mirtec machine for 3 years MV3L with side angle inspection. Mirtec has some issues documentation, and repair plus. But there machine is impressive and the AOI software is good. We can find about 90-99.99% of all errors using just the 5
Electronics Forum | Tue Aug 22 21:00:39 EDT 2006 | davef
National says: [ http://www.national.com/packaging/llp/faq.html#faq_manu ] Manufacturing FAQ's Are there any precautions that need to be taken with the LLP package? It is critical to follow National�s guidelines for successful surface moun
Electronics Forum | Wed Apr 21 22:15:12 EDT 1999 | Chris
| I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is abo
Electronics Forum | Tue Dec 08 17:55:51 EST 1998 | Dave F
1. What is the best way to remove polyurethane conformal coating from selected areas? Your conformal coat material supplier is best equipped to tell you how to remove the coating. Polyurethane conformal coating is not easy to remove. Without in-pu