Electronics Forum | Fri Jun 25 08:38:37 EDT 2010 | mun4o
Thanks, Dennis. That is a good idea, but I have problem :) - our logistic department lookig for cheap components...What other mnfg of cap you use? Regards,
Electronics Forum | Wed Jun 23 08:47:32 EDT 2010 | mun4o
Hi, about location - components are in the diferent location on PCB.In the one PCB have 7 cap 560pF 0603 , and some of thenm are cracked, another are OK. When I look at 20x microscope , I can't see defect, but ICT measure from 200 to 350pf.When hea
Electronics Forum | Fri Jun 25 09:18:23 EDT 2010 | flipit
Thanks, Dennis. That is a good idea, but I > have problem :) - our logistic department lookig > for cheap components...What other mnfg of cap you > use? Regards, The capacitor dielectric material might be something you could look at also. COG,
Electronics Forum | Fri Jul 09 19:09:52 EDT 2010 | rway
A couple of things: Does the cap break if you try to remove it with hot air? If not, than you are breaking the caps do to mechanical stress. We have had similar issues. I don't think your board is suffering from mechanical stress from depaneling o
Electronics Forum | Thu Mar 14 09:07:26 EST 2002 | cfraser
I can not tell you what the actual stress limits are. I can tell you that de-paneling PCB's by hand is a very poor choice. I have seen numerous accounts of cracked caps, resistors, and LED�s due to incorrect de-paneling procedures. I would recommend
Electronics Forum | Fri Aug 27 12:28:34 EDT 2010 | patrickbruneel
Under certain circumstances, Toyota says, solder connections may develop a crack that creates unpredictable behavior in the circuit. Look here: http://www.thecarconnection.com/marty-blog/1048692_toyota-recalls-1-1-mi
Electronics Forum | Tue Apr 13 08:21:05 EDT 2010 | esca
Hi manchella, After ATC test, two different failure modes can be present: solder FATIGUE (into bulk) or BRITTLE INTERMETALLIC fracture. So, first you have to verify this. Moreover, which brand of SMT paste have you used ? The crack into solder joint
Electronics Forum | Sun Apr 11 11:39:52 EDT 2010 | manchella
When we have sent some of motherboards for reliability testing in a tird party laoratory. It is found that when Dye&Pry is done after 600 cycles of Thermal Cycling, in LGA socket only one of the corner solder joing had 100% type 3 crack. All other so
Electronics Forum | Tue Feb 16 12:44:05 EST 2010 | esoderberg
95%+ of my boards are small and therefore are panelized using the V-score technique. Getting a lot of resistor cracking even though the resistor is layed out to be perpendicular to the long board edge. What dimension should be used from the board e
Electronics Forum | Tue Feb 23 09:48:26 EST 2010 | dyoungquist
How are you sepatating your boards out of the panel? If you are flexing them to break the V-score, this could be what is causing the resistors to crack.