Electronics Forum | Mon Jun 12 13:10:05 EDT 2006 | muse95
Why do they say to specify the depth of the score, rather than the thickness of the web? How does the scoring equipment work? Is it two blades that you can set the separation distance? Or is it one blade, that you have to run the board through twic
Electronics Forum | Mon Jun 12 14:31:08 EDT 2006 | russ
As far as wich is spec'd it makes no diiference since they have reltionship with each other, Cant change one without the other. V score equipment I have seen is one blade and they are run through twice. their may very well be that there are dual b
Electronics Forum | Mon Jun 12 14:33:40 EDT 2006 | pjc
IPC spec is V-score shall not be more than 1/2 board thickness. They should be V scoring 1/4 off top and 1/4 off bottom equally.
Electronics Forum | Mon Jun 12 16:33:39 EDT 2006 | muse95
Which spec is that in? I'm seeing web thicknesses of .015 or thinner being suggested for a .062 board, way thinner than 1/2 the board thickness.
Electronics Forum | Tue Jun 13 08:33:11 EDT 2006 | davef
IPC-2222, 5.3.1 defines the parameters of making scoring cuts and the tolerance of the cuts, but does not specify the cuts. Our spec for 0.062" thick FR-4 boards is: 0.018-0.024"
Electronics Forum | Wed Jul 05 10:13:02 EDT 2006 | jdengler
Is the flux rated for lead free? These higher temps will cause most lead rated fluxes to burn off prior to the wave. Jerry
Electronics Forum | Wed Jul 05 13:30:37 EDT 2006 | Chris Griffin
Likely causes of this are: -Preheat temp. too low -too much dross -uncured epoxy -PCB contamination ...also varify the solder flow over the wave is smooth.
Electronics Forum | Thu Jul 06 04:41:58 EDT 2006 | Rob
MF300S is quite an old flux, & a lot has happened since then on the flow solder front - are you sure it's designed for Lead free, or is it just a traditional flux that SHOULD work OK with Lead free?
Electronics Forum | Thu Jul 06 12:26:55 EDT 2006 | Chunks
Sounds like your flux to me. Since you cannot change the board or the machine, changing flux would be one question mark you could take away with a phone call and a sample. You will really be surprised how different fluxes can affect your final prod
Electronics Forum | Mon Jul 10 07:46:51 EDT 2006 | ronalds
You are right, RSS profile is not the correct description. I am using a profile which heats up quickly to let the flux spread. Next linear up to activate the flux and prevent thermoshock. My experience is however, that small changes in this profile