Hybrid flux: No-clean and WS

Electronics Forum | Wed Jul 12 19:13:18 EDT 2006 | russ

i have heard of washable no-cleans for about 6-8 years now. I would think that if SIR values are acceptable for end use then I would run with it. Russ

Thanks and happy holidays everyone

Electronics Forum | Fri Dec 22 12:35:11 EST 2006 | bvdb

Happy holidays to all and many thanks to those people who helped me and others during the year! I really enjoy reading the interesting posts and have learned a lot from them. Regards, Bert van den Berg

Thanks and happy holidays everyone

Electronics Forum | Sat Dec 23 06:31:19 EST 2006 | Grant

Hi, I agree, and I would be in trouble without everyones kind help on this forum! Merry Christmas and I hope everyone has a great new year! Regards, Grant

AOI selection,specifically ViTechnology and Mirtec

Electronics Forum | Mon Jul 17 13:36:55 EDT 2006 | kjeffries

I appreciate your comments regarding the programmability of the Mirtec. What type of SMT machine do you use? How easy have you found it to transfer the SMT profiles to the Mirtec? How do you rate the Mirtec in handling top/bottom, multi-panel asse

AOI selection,specifically ViTechnology and Mirtec

Electronics Forum | Tue Jul 18 00:47:42 EDT 2006 | sant

Hi Few weeks back for the similar thread I was enquiring about the performance of benchtop AOI. I did see the Saki m/c.It seems to be a good m/c with different technology. I have not bought yet. Looking to have more feedback. Any opinion about Saki

Heat guns and component damage

Electronics Forum | Tue Jan 31 14:30:38 EST 2006 | Chunks

There is none, since we don't know your part or temp being used. A heat gun CAN be used to remove parts with no damage, if its controled. You need to look up your part on the manufacturers web site, find the process data (time/temp)the part is desi

Heat guns and component damage

Electronics Forum | Tue Jan 31 14:58:15 EST 2006 | samir

You see? Chunks, here has the right idea! To the original poster, you need to show this post to your "Desk Jockey" Process Engineer. That's the problem with some Engineers today. They forget everything they learned in Engineering school, they get

Heat guns and component damage

Electronics Forum | Tue Jan 31 15:40:44 EST 2006 | mgdrouin1

Comp is relay. I've pulled the spec. Max 240. Using Leister h/g with manual temp settings from 1-6 (20 - 600C)set by the operator. Gun was set to setting 4. They are using the heat gun to reflow the solder after SMT but before wave. High fai

Heat guns and component damage

Electronics Forum | Wed Feb 01 22:27:16 EST 2006 | KEN

Many relays use soldered post coil terminatins inside the relay. In one case many years ago I found the SMT relay manufacturer used eutectic solder inside their hermetic relay. The SMT relay would fail because the solder balled up on the post, woul

Stencil and board Ultrasonic cleaner

Electronics Forum | Wed Feb 01 13:32:18 EST 2006 | samir

Whatever you do, don't get a cleaner where they "lock" you into using their Saponifier! I remember at my previous company, getting that monstrosity running was my 1st project - the boob who bought it washed his hands of it and assigned it to me.....


20in and 2006 searches for Companies, Equipment, Machines, Suppliers & Information

Online Equipment Auction of Altronic: Small-Batch Surface Mount & Assembly Facility

High Precision Fluid Dispensers
Conductive Adhesive & Non-Conductive Adhesive Dispensing

High Throughput Reflow Oven
PCB Handling Machine with CE

World's Best Reflow Oven Customizable for Unique Applications
Baja Bid Auction JUL 9-10, 2024

Reflow Soldering 101 Training Course