| | | I have been involved in SMT for only a few months so I am coming from a position of extreame ignorance. I have been asked to investigate the differences in soldering to components with Paladium coated leads vs the standard Tin_lead. I would
Electronics Forum | Wed Feb 25 12:55:23 EST 1998 | N.J Bateman
| | | I have been involved in SMT for only a few months so I am coming from a position of extreame ignorance. I have been asked to investigate the differences in soldering to components with Paladium coated leads vs the standard Tin_lead. I would
Electronics Forum | Fri Dec 12 11:52:59 EST 2003 | Marc Simmel
I have encountered problems with a 90/10 tin-lead plated SMT component wicking all the solder paste off the pads on the substrate. Worst, the defect occurs randomly - adjacent leads may have 'good' joints, though heel fillets are poor. The solder pa
Electronics Forum | Thu Sep 07 10:39:34 EDT 2006 | vicknesh28
Can u elaborate on the bad plating? Have u had any experience on this before? The component has 90/10 Tin lead plating
Electronics Forum | Tue Feb 14 13:16:49 EST 2006 | Carol Stirling
CRITICAL DILEMA! Has anyone run into the problem described below and if so, what was the fix (besides not dealing with this Supplier)? Also, we do not have component manufacturing process experience. We are purchasing a surge resistor that function
Electronics Forum | Tue Dec 23 11:55:37 EST 2003 | Marc Simmel
Details, details: 1) The metal shell is part of the component body. The base metal is austenitic stainless steel (304) that has been plated with 90/10 tin-lead over nickel (semi-bright). 2) The entire part (leads and shell) is elevated by the mass o
Electronics Forum | Tue Apr 13 09:11:54 EDT 1999 | Dave F
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Thu Apr 22 17:19:57 EDT 1999 | JohnW
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Tue Aug 31 21:45:49 EDT 2004 | KEN
I have experienced this directly in SMT and wave solder. Fillet lift (can) be a direct indicator to lead enrichment (but its not the exclusive symptom). Lead enrichment in smt joints reduces the interfacial strength shortening the time to creep f
Electronics Forum | Mon Apr 23 15:44:31 EDT 2007 | flipit
Steve, You read it the same way I read it. Some of my coworkers thought that the 600 micron and under spec meant that you could use lead solder and be exempt at this component pitch. That is why I posted it on SMTNET. The exemption specifically s
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
Building A, Jiepeng Square, Fuyong
Shenzhen, 30 China
Phone: 0755-33578694
.jpg)
.png)