Electronics Forum | Wed Apr 25 15:19:15 EDT 2007 | flipit
Steve, See the link below. See the out take from the link below. http://forum.europa.eu.int/Public/irc/env/rohs/library?l=/requests_exemptions/resistant_applications/hpdoc/_EN_1.0_&a=d The specific verbiage is, "This exemption request seeks to
Electronics Forum | Fri Aug 07 07:52:15 EDT 1998 | Earl Moon
| | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not e
Electronics Forum | Mon Aug 10 21:52:34 EDT 1998 | Dave F
| | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not
Electronics Forum | Tue Aug 11 07:51:57 EDT 1998 | Earl Moon
| | | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, n
Electronics Forum | Wed Aug 12 07:22:52 EDT 1998 | Earl Moon
| | | | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated,
Electronics Forum | Mon Mar 01 12:50:47 EST 1999 | justin medernach
| Hello! SMT professionals, | | I do not know if anyone posted this question before. | Last week, I reflowed our newly designed thin Rigid-Flex pcb with 0.040" thickness. I found all of pins of a TQFP48 ic did not get wetted. I could see on the hee
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Fri Jul 30 16:02:49 EDT 1999 | Earl Moon
| | I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. | | This ceramic su
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
Building A, Jiepeng Square, Fuyong
Shenzhen, 30 China
Phone: 0755-33578694