Electronics Forum | Thu Aug 18 20:10:06 EDT 2016 | souldierann
Hi SweetOldBob, how did you say then?
Electronics Forum | Fri Sep 09 05:32:11 EDT 2016 | jasltd
Are your solder relief pads connected to anything in terms of ground planes that would increase the thermal load or are they floating copper? I take it your talking about wave solder relief pads?
Electronics Forum | Mon Jan 15 14:25:54 EST 2001 | davef
Let me make several points on this issue � POINT 1: Let�s be basic � Soldering and welding are examples of process that the quality types call "special processes". Special process. The results of special processes cannot be verified fully by subs
Electronics Forum | Fri Jan 19 12:17:57 EST 2001 | slthomas
Thanks Dave. Talked to a few people at APEX this week and if nothing else, had my frustration reduced some. Of course I made sure I talked to mfg. people and avoided the design guys like the plague. ;) I actually picked up a copy of 785 a while bac
Electronics Forum | Thu Nov 20 06:50:36 EST 2008 | caerleon
I always thought that the use of palladium was specifically for conductive epoxies!?!
Electronics Forum | Mon Dec 01 05:40:48 EST 2008 | jandon
We have same problem with Burr Brown OPA277UA.
Electronics Forum | Tue Nov 18 19:14:04 EST 2008 | swag
We had very similar solderability problem with TI P/N SN74LVC2G34DCKR.
Electronics Forum | Wed Nov 19 14:08:55 EST 2008 | stepheniii
TI was leadfree before ROHS. I saw TI solderability issues over 10 years ago. The leads have paladium and need higher reflow temperatures.
Electronics Forum | Tue Nov 25 12:33:57 EST 2008 | jdumont
We had the same issue with the INA121's a while back if im not mistaken... i believe the design was changed do to other reasons with that part and the prob went away.