Electronics Forum | Thu Jan 17 20:33:05 EST 2002 | ianchan
Hi, Can anyone help explain the benefits/disadvantages of bareboard pcb baking, as part of the pre-heat conditioning, before the bareboard pcb use in SMT production run? The pcb board is 200mm x 240mm panelized pcb board, and has 28 smaller pcb boa
Electronics Forum | Thu Apr 20 22:14:51 EDT 2006 | raquel
hello! need ur inputs... if the Matte Sn pbfree finish of the component discolors AFTER having been exposed to bake, or, after reflow, will the base leadframe have any potential contribution to it? i know most likely suspects would be the plating pro
Electronics Forum | Fri Nov 05 21:22:34 EST 1999 | chartrain
Amazing in today's technology that people still bake because "that's the way we've alawys done it". Baking is a band aid for poor manufacturing of the PCB. Moisture can become trapped between the layers during buildup. This moisture when it contacts
Electronics Forum | Mon Apr 26 14:40:07 EDT 2010 | blnorman
We had one product that used immersion silver plating. There were a couple of instances where we saw tarnishing, and elemental analysis confirmed the presence of sulfur. These boards did have the anti-tarnish sheets between boards, but somehow they
Electronics Forum | Mon Aug 25 12:18:10 EDT 2008 | evtimov
I am looking for an inexpensive way to bake just > a few components. would a toaster oven be okay on > the low setting (i would get a thermometer!) do i > need to get something to place the components on? > maybe a silicon cooking mat (not sure a
Electronics Forum | Fri Apr 23 17:59:54 EDT 2010 | hegemon
Therein lies the issue. Unknown storage conditions before we received the PCBs, date codes just expired (2 weeks), first article is de-lam city! Had a bad feeling about it. Have read some studies showing that there is no linear tie in of visual cha
Electronics Forum | Thu Jun 08 09:43:42 EDT 2017 | davef
You know the scary part about your mentioning a tread where I post something? Well. let's just say that 2007 was a long time ago. Anyhow, silver will dissolve into your solder and provide no barrier. Some people apply a silver flash plating over the
Electronics Forum | Wed Sep 12 16:15:28 EDT 2007 | rpadilla
Does anyone have Data/Comparisons showing which component plating is better, Nickle plating vs. Sucoplate for SMT production? These components would be reflowed with a SAC305 alloy
Electronics Forum | Thu Dec 18 17:10:01 EST 1997 | Tom Volker
I am designing an SMT pad for a ss metal switch. Finished copper thickness is .0014 and nickle-plating originally is 150 millionths. Initial testing yields 100,000 to 150,000 switches before intermitent failures (copper is reached.) I want 500,000
Electronics Forum | Sat Mar 21 09:09:40 EDT 2009 | davef
Your puzzlement about blowholes in PTH solder connections during reflow soldering comes from: * Boards are hydroscopic. So, moisture content of the board is uniform. * Gold plating is uniform. * Nickle plating is uniform. * Copper plating on your PTH