Electronics Forum | Thu Mar 30 11:07:41 EST 2000 | Wolfgang Busko
> the dirty patch appear seems to be a bit powdery on top of stickiness > the "harden" dirt in the solder pot or at pump are ususally "knock" out while cleaning.. is that thorough enough..? Assuming that 1) is true it might not be thorough enough. On
Electronics Forum | Thu Mar 30 04:42:28 EST 2000 | cpgoh
HI all, thanks for the advise.. Electrovert is being used from 7am to 7pm and we do dedross from the surface of the solder bath during lunch time around 12nn. Break Time we just sweep them to the side.. Every two week, we do the solder bath maintena
Electronics Forum | Sun Sep 09 08:38:14 EDT 2018 | devinpcb
I have found the paste flux is the worst. It leaves a black residue that can corrode.
Electronics Forum | Fri May 23 23:58:48 EDT 2014 | edriansyah
Hi Hege. I was not also too confident with the black pad (coz no black residue on the remaining pad). But based on my search on the internet regarding black pad. Most of them shows a very clean BGA Pad after peel off the BGA as the picture reference
Electronics Forum | Mon Dec 18 04:11:11 EST 2006 | greg york
Probably because the flux manufacturers have deemed it necessary to increase flux volume by 20 - 25% compared to Leaded this is why more is being left over. Really not convinced of this increase in volume actually does anything. Black residue will be
Electronics Forum | Sat Jul 21 00:38:46 EDT 2001 | dougk
Where did this come from? I hope our safety director doesn't see this or I'll have more work to do. Seriously, if is bacterial contamination, it would be lysed immediately on contact with the iron. We ask our operators to wash their hands after handl
Electronics Forum | Fri May 21 15:36:05 EDT 2010 | ccross
That is exactly the type of problem we are having. Some work, some dont. We feel these parts are not counterfeit so to speak but reworked, removed from other boards, cleaned up to some degree - hence the flux residue, black contamination, scrapes, wr
Electronics Forum | Fri Dec 08 21:23:16 EST 2006 | Harsha
I am seeing a problem of flux droping on the PCBA during reflow. This is a pb free process and I am using KOKI pb free paste with 8 zone (and some 9 zone) reflow ovens. Line throughput is about 10,000 boards/24 hours. I suspect that the exhaust is no
Electronics Forum | Sat Oct 09 03:45:34 EDT 1999 | Brian
| Right now,we have some problem on SMT. Cause of the flux residue | in the connector. Do somebody have the same symptom? By the way, | can i find something to make the flux observe easy or take a photo with the flux. | | | Unfortunately, this pr
Electronics Forum | Fri Feb 23 17:35:49 EST 2001 | mattias
Ok. F.Y.I How I could make this work: We use Almit V14, and SMT ovens. You can say that we don�t do our maintenance as good as we should. Our Smt Quattro peaks are equipped with process gas cleaning (wich works quite good actually) I ripped out the