Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Wed Feb 09 21:37:37 EST 2000 | Dave F
Rob: Someone's out there turning over stones, eh? Roller Tinning, Rolled Solder. In printed circuit fabrication, a surface coating of tin-lead, typically 1-2 microns thick, applied to preserve solderability. Still available from some fabricators
Electronics Forum | Fri Jan 14 07:55:07 EST 2000 | Pat Pepper
Hi Wolfgang, Thanks for the response. We had a similar situation to yours with some white tin samples that sat around for about eight months. Samples soldered right after they arrived soldered better than the ones we soldered eight months down the
Electronics Forum | Wed Feb 12 12:06:58 EST 2003 | dwanzek
I need some input on what good solder thieves dimensions should be. I am limited to solving my bridging problem with solder thieves; all process/wave variables have been adjusted to try to solve this problem. There are several of these connectors on
Electronics Forum | Wed Feb 12 13:37:22 EST 2003 | dwanzek
I need some input on what good solder thieves dimensions should be. I am limited to solving my bridging problem with solder thieves; all process/wave variables have been adjusted to try to solve this problem. There are several of these connectors on
Electronics Forum | Fri Jun 18 13:48:37 EDT 1999 | Earl Moon
| We currently use HASL on all of our boards and I would like to move to something else. I have sampled some boards with Entek OSP and I loved it, the problem is we have plated mounting holes on just about every board we make. Does anyone have info
Electronics Forum | Tue Mar 10 22:16:56 EST 1998 | Steve Gregory
Jeremy, I'm gonna make a couple of assumptions by "reading in between the lines" of your email: 1. You're using no-clean paste. 2. This is only happening on the second side. You tell me if I'm wrong about this... First thing, if you're only experienc
Electronics Forum | Thu Feb 03 21:17:07 EST 2000 | Dave F
AF: Unfortunately, there is no "acceptable number of cycles" either in air-to-air and one liquid-liquid thermocycling, nor interconnect stress testing. There can be a "minimum threshold" that would assure no failures as the result of the assembly p
Electronics Forum | Fri Feb 19 11:28:51 EST 1999 | Steve Gregory
Hi Bob, I know what you're talking about, it seems that most machines that I've worked with, have at one time or another some problem seeing a fiducial. Some machines are worse than others, and it really didn't make a difference what kind of vi
Electronics Forum | Wed Jan 13 04:27:00 EST 2016 | crystalpcb
Hi Here is our factory production capability: Shenze Electronic PCB Specification Layer Count 1 to 35 Layers Material Brand Shengyi,KB,GRACE,ISOLA,Rogers,Taconic,ARLLON,Bergquist Base Material FR-4（TG135,TG150,TG170,TG180），Halogen Free FR-4，Ceramic