Electronics Forum | Thu Sep 07 07:41:06 EDT 2006 | Bubba
Check for coplaner leads if this just exists at reflow process, i.e. look at part before oven, turn on 3D at placement machine. If you see after wave solder, the wave could cause coplanarity issues on top as well if you are going slow enough to refl
Electronics Forum | Thu Jan 09 13:18:15 EST 2020 | charliedci
We have been experiencing an issue with solder balls coming out of wave, both RoHS and 63/37, no clean process. It has been determined that a reduction in flux has all but eliminated the solder balls except for where we need to use board stiffeners a
Electronics Forum | Tue Apr 25 13:05:08 EDT 2006 | Hoss
TMC, Are you interested in this approach because you only have a flat belt conveyor and want to keep the components from being moved by the belt on the second pass? If so, you might try adding some stiffeners to the board edges to stand the board o
Electronics Forum | Tue Jun 17 15:52:51 EDT 2003 | russ
Is this a single sided or double sided board? We run the first side flat on the oven belt this keeps the board flat for the second side assembly. If the board warps during the second reflow process we will make a support fixture to carry the PCBA
Electronics Forum | Mon Jul 01 09:33:08 EDT 2019 | dbuschel
if you can't change the PCB materials or design at this point, you might be able to reduce it somewhat through the use of fixtures or edge stiffeners. Unless it is a particularly thick board, I don't think the reflow profile would be the issue. The t
Electronics Forum | Thu May 07 21:25:56 EDT 1998 | D.Lange
| I am running a board that is .062" thick and has components that over hang the edge of the board by .090". I have bottom side smt components (chip caps and resistors only) and use the turbulent wave to help solder the components. The problem I am
Electronics Forum | Thu Jun 17 10:25:43 EDT 1999 | Brian Wycoff
| | We are a medium sized PCB assy. house manufacturing about 2000 motherboards a day. There is a major problem we are facing at the wave soldering stage, i.e. warpage of the PCB. As soon as the PCB touches the wave it warps severely from the centr
Electronics Forum | Thu May 07 12:29:17 EDT 1998 | Rob Williams
I am running a board that is .062" thick and has components that over hang the edge of the board by .090". I have bottom side smt components (chip caps and resistors only) and use the turbulent wave to help solder the components. The problem I am h
Electronics Forum | Tue Jul 17 18:19:09 EDT 2001 | dave
CONNECTOR, 4 X 40, MALE, SM, 0.472 STANDOFF301-00030TOLC�Mount(1,27mm),.050",(0,64mm) .025",micro pitch Looking for someone who has had experience placing this Samtec style of connector .We are having issue with open solder and insufficent. We are no
Electronics Forum | Mon Aug 27 15:03:40 EDT 2001 | davef
Essentially, you want to ruggedize this component. Various adhesives could work great, depending on the source of the energy that is causing the solder connection fatigue. So, what are your looking to: * Rigidly bond the component to the board? * A