Electronics Forum | Mon Jan 07 20:37:15 EST 2002 | davef
For soldered areas, we like to keep gold thickness substantially below the maximum you propose. Search the fine SMTnet Archives for our discussions on the topic of acceptable levels of gold with solder connections. Let�s fix this �no one seems be s
Electronics Forum | Fri Aug 17 11:55:31 EDT 2001 | davef
5uin. Your nickel thickness is fine. Although if you wanted to trade costs, consider giving-up nickel to 150uin thickness, while increasing the gold thickness. Gold over electroless nickel creates brittle joints because of phosphorous in the nicke
Electronics Forum | Fri Apr 17 21:46:18 EDT 1998 | Matthias Mansfeld
I plan to design a multichip module which contains 1 chip with about 200 pads and 2 chips with about 50 pads, no other components.The whole module shall replace as intermediate solution a single chip CPU in QFP208. Thus, the MCM itself must have t
Electronics Forum | Wed Mar 10 15:45:24 EST 2010 | flipit
Looking for a large area wire ball bonder or wedge bonder. Must be able to take 4" X 5" panel and have a bond area of close to 3.5" X 4.4". Also need 6 to 8 wire per second. K&S no longer makes one. Panasonic no longer makes one. ASM does not mak
Electronics Forum | Tue Mar 16 18:36:11 EDT 2010 | janz
Looking for a large area wire ball bonder or > wedge bonder. Must be able to take 4" X 5" panel > and have a bond area of close to 3.5" X 4.4". > Also need 6 to 8 wire per second. K&S no longer > makes one. Panasonic no longer makes one. ASM
Electronics Forum | Tue Jan 30 17:58:49 EST 2007 | flipit
Hi, I would not be too concerned about what the shape of your wirebonding fiducial is. Cross, Square, Diamond, Circle, will all work well for you. I use a "+" and a diamond. Your machine magnification will be great, so don't make the fiducials to
Electronics Forum | Fri Aug 17 01:40:55 EDT 2001 | V.RAMANAND KINI
We are in the watch & clock Business. We have a Watch IC chip that has to be wirebonded using Ultrasonic aluminium wedge bonder. The wire dia is 1.25mil. The PCB is made of G10 Glass epoxy copper clad laminate. The copper thickness is 18 microns. The
Electronics Forum | Mon Aug 27 15:06:29 EDT 2001 | davef
This otta push Wolfgang over the top ... Recommended reading G.G. Harman, Wire Bonding in Microelectronics : Materials, Processes, Reliability, and Yield, 2nd edition, McGraw-Hill Electronic Packaging and Interconnection Series, 1997. G.G. Harman, R