Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Wed Aug 12 07:22:52 EDT 1998 | Earl Moon
| | | | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated,
Electronics Forum | Thu Sep 30 12:29:01 EDT 1999 | Dave F
| Hi everyone, | | Greetings! | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | Insufficient Solder and some solder ne
Electronics Forum | Thu Sep 30 21:37:44 EDT 1999 | Dreamsniper
| | Hi everyone, | | | | Greetings! | | | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | | Insufficient Solder an