Electronics Forum | Mon Jan 19 22:59:52 EST 2015 | mac5
Carl, You can use a high temp solder to connect your T/C's but we use Kapton or glass tape so the T/C's can be reused. Mac
Electronics Forum | Thu Sep 16 21:27:42 EDT 2004 | Darby
Dymo labelmaker with the help of Loctite 401. You can remove later to reuse the frame with a Stanley knife. Works well for me with a similar storage system.
Electronics Forum | Thu Sep 21 15:33:52 EDT 2000 | Gilbert Ramirez
We currently use process carriers to run our products. We do not have chillers at the end of the reflow ovens (no space) so you can imagine how hot the carriers come through. Are there any cooling racks out on the market that I can look into to pla
Electronics Forum | Wed Oct 04 17:29:53 EDT 2023 | SMTA-72837649
Can you order a blank thin pcb to use as a carrier?
Electronics Forum | Mon Jun 18 10:34:40 EDT 2007 | swag
If you are using a fixture/carrier in the oven, make sure that it is not too restrictive on the perimeter of the board/panel. A carrier intended to limit warpage can actually cause warpage if the expanding PCB material has no place to go during refl
Electronics Forum | Thu Jun 05 10:17:12 EDT 2014 | swag
Can you cut v-scores deeper to resolve the issue then build carriers to support the panel? I would say that we usually build carriers for anything that thin regarless of the depanel method.
Electronics Forum | Tue Feb 20 16:33:08 EST 2001 | davef
Time, time, time. There just never seems to be enough!!! Eh? You�re correct. Depending on the material, some trays can take a high temperature bake, while other trays, in addition to tubes, and reels, require a low temperature bake. With this la
Electronics Forum | Sat Feb 26 09:22:19 EST 2000 | Dave F
Jason: Assuming you wantto reuse the TSOPs, two things come to mind: 1 Don't bend the leads. This can be caused by not melting the solder on all leads at the same time. 2 Don't break the body. This can be caused by moisure absorbed by the case ex
Electronics Forum | Sat Feb 26 09:22:19 EST 2000 | Dave F
Jason: Assuming you wantto reuse the TSOPs, two things come to mind: 1 Don't bend the leads. This can be caused by not melting the solder on all leads at the same time. 2 Don't break the body. This can be caused by moisure absorbed by the case ex
Electronics Forum | Mon Nov 03 03:20:25 EST 2003 | magdelectronics
Hello Cal, I have left Tempo and started my own business. We manufacture a carrier tape like that of Surftape. Mag-D Electronics Adhesive Back Carrier Tape has a punched Blue Nitto Tape Gap and not two rails. Our Punched Nitto carrier is more acc