Electronics Forum | Fri Apr 04 14:54:19 EDT 2008 | alexs
Thanks for the reply. Just one more question. If there is less solvent but the residues are harder to clean. would there be more contaminant left on the boards? Has anyone did a cleanliness test?
Electronics Forum | Mon Jan 18 19:53:58 EST 1999 | Rob F
| | I'm in the process of moving from water washable flux to a full no clean process for the wave soldering process, thing's seem to be going well (so far...). | | The one problem I still have is cleaning the wave solder carrier's to remove the no cl
Electronics Forum | Fri Jul 06 03:23:01 EDT 2001 | kennyhktan
Hi there Steven ! Please allow me to share some of my problem we're facing here with you. Here are a few points that I suggest you should check on your current process:- (1)PCB - Component land partern design ? It is per IPC spec ? - Mask
Electronics Forum | Thu Jul 15 19:05:58 EDT 1999 | Earl Moon
| | | We have been encountering diminishing ball shear readings these past few weeks, despite the fact that we did not change any ball shear tester parameter. Our reflow parameters are also within spec limits. ( 210-220 deg C max temp. and 40-60 sec
Electronics Forum | Fri Jan 08 10:07:26 EST 1999 | Chrys
| I'm in the process of moving from water washable flux to a full no clean process for the wave soldering process, thing's seem to be going well (so far...). | The one problem I still have is cleaning the wave solder carrier's to remove the no clean
Electronics Forum | Thu Mar 29 18:14:19 EST 2001 | kerryn
Hi Dave, I looked into the South Coast Air Quality Management District Clean Air Solvent Certification when I was having my problems with VOCs. The problem with the SCAQMD CAS Certification is that it only certifies chemicals as they are found in t
Electronics Forum | Fri Sep 09 15:53:22 EDT 2005 | patrickbruneel
If the white residue is from a no-clean flux or no- clean solder flux core you can leave it on the board. (Consult with the flux or cored solder manufacturer) Because after being encapsulated with conformal coating the residue is sealed from humidity
Electronics Forum | Wed Mar 20 15:17:38 EST 2002 | MikeF
I understand your point, and generally agree with you about no lotions in the production area. My question for you and the others is what to do with the person whose skin is so dry it does not make good contact with their ESD wristband? I do not li
Electronics Forum | Tue Aug 08 14:50:41 EDT 2006 | mumtaz
Yes yes Wss, I could not agree more. Many people like to put others down because they post here. Making sense of others problems boggles there minds and they turn confusion into rage. Let me start by saying Larry Wave Master alway posts crazy sh
Electronics Forum | Wed Mar 09 08:23:31 EST 2005 | davef
We don't have experience on this, but first we'd talk to a technical type at our solder paste supplier. Baring that, we'd: * Soak a paper towel in a 'solvent' [ie Kyzen XJN, EnviroSense Enviro Gold, Petroferm Hydrex, etc]. * Place the towel in conta