Electronics Forum | Thu Aug 05 06:29:18 EDT 1999 | Graham Naisbitt
| | | We're getting field failures in a high impedance portion of the circuit. Think the unpopulated pc card has contaminates because we were able to grow dendrites by applying a 9 volt battery across the suspected pad, placed a drop of de-ionized w
Electronics Forum | Tue Sep 19 09:41:30 EDT 2017 | sumote
Steve, The 4 things I would do, and in this order: 1. Clean your stencil with stencil cleaner wipes after it comes out of the stencil cleaner. I like MicroCare ProClean (MCC-PROWR). I will even saturate the wipe with a bit of isopropal just till
Electronics Forum | Tue Aug 31 13:23:37 EDT 2004 | frankracine
Thanks Ken for your reply. Concerning OSP, there are a few negative points that I must considered for our application. I've read all the following points in an Entek document. Never test it. - If you have a miss print and you clean the PCB, the co
Electronics Forum | Fri Jun 01 10:52:37 EDT 2012 | blnorman
Neither the Omega meter nor the IC are officially "destructive" tests, but everywhere I worked we treated them that way. The boards were scrapped after the test. The Omega meter can be tested at elevated temps, but the IC sample is extracted at ele
Electronics Forum | Wed Feb 16 21:51:29 EST 2000 | Dave F
Kurt: Lots of choices, not many of them good, yano. 1 So LPI has taken over the market pretty nearly 100%, but it won't "tent" reliably, because it is not very viscous when applied and drops into the hole. So then, tenting/plugging with LPI is bad
Electronics Forum | Wed Feb 16 21:51:29 EST 2000 | Dave F
Kurt: Lots of choices, not many of them good, yano. 1 So LPI has taken over the market pretty nearly 100%, but it won't "tent" reliably, because it is not very viscous when applied and drops into the hole. So then, tenting/plugging with LPI is bad
Electronics Forum | Sat Oct 06 08:32:09 EDT 2001 | davef
Mr. Wizard is not currently available. You get the wizzer. Maybe your dream date will show later. Get your own lab tests done. Show your potential customer that your boards are clean. That�s the issue. The issue is not how you go about cleaning
Electronics Forum | Thu May 09 17:13:10 EDT 2002 | davef
We are converting all our ENIG to imm silver. CHARACTERISTICS * Nominal thickness of the deposit will be 0.1 to 0.3 microns. * Deposit is flat and uniform * It will withstand multiple heat cycles in assembly, which can be problematic with tradition
Electronics Forum | Mon Apr 06 12:32:20 EDT 1998 | Roxanne Picou
March 31, 1998-Austin, TX --- Austin American Technology announces a new Pre-Wash feature for the Mega� II to operate in conjunction with AAT's patented closed-loop regenerative cleaning process. This feature allows for an optional dual chemistry
Electronics Forum | Mon Oct 16 20:29:32 EDT 2000 | Dave F
Jason: How did you determine that the deposits are tin oxide? What does this stuff look like? Klein Wassink "Soldering in Electronics" (p. 221, quoting original work by others). States (in effect) tin (or solder) quickly forms a protective oxide