Electronics Forum | Mon Nov 13 11:31:10 EST 2000 | John Rep
I am having a problem with wetting on some feedthru wires. The problem seems to be contamination on the wires, due to the fact that the problem seems to be wire lot dependent. I have analysed it using SEM and come up with very little. Is there ano
Electronics Forum | Thu Apr 15 08:23:47 EDT 2004 | prod
hi, Having put a copper socket trough a wave soldering machine, and then through a DI wash, the boards have been dried and after a few days a green residue has been noticed on the copper. any suggestions? not drying properly maybe? or could it be th
Industry News | 2010-09-13 15:36:15.0
IPC — Association Connecting Electronics Industries® has released IPC-1601, Printed Board Handling and Storage Guidelines. The industry's sole standard on the handling, packaging and storage of printed boards, IPC-1601 provides users with guidance on how to protect printed boards from contamination, physical damage, solderability degradation, electrostatic discharge and moisture uptake.
Industry News | 2011-02-24 20:35:03.0
The SMTA is pleased to announce the program for the 2011 International Conference on Soldering and Reliability being held May 3-6 in Toronto, Ontario, Canada.
Technical Library | 2018-05-09 22:15:29.0
Creep corrosion on printed circuit boards (PCBs) is the corrosion of copper metallization and the spreading of the copper corrosion products across the PCB surfaces to the extent that they may electrically short circuit neighboring features on the PCB. The iNEMI technical subcommittee on creep corrosion has developed a flowers-of-sulfur (FOS) based test that is sufficiently well developed for consideration as an industry standard qualification test for creep corrosion. This paper will address the important question of how relative humidity affects creep corrosion. A creep corrosion tendency that is inversely proportional to relative humidity may allow data center administrators to eliminate creep corrosion simply by controlling the relative humidity in the data center,thus, avoiding the high cost of gas-phase filtration of gaseous contamination. The creep corrosion relative humidity dependence will be studied using a modified version of the iNEMI FOS test chamber. The design modification allows the achievement of relative humidity as low as 15% in the presence of the chlorine-releasing bleach aqueous solution. The paper will report on the dependence of creep corrosion on humidity in the 15 to 80% relative humidity range by testing ENIG (gold on electroless nickel), ImAg (immersion silver) and OSP (organic surface preservative) finished PCBs, soldered with organic acid flux.
Technical Library | 2013-02-07 17:01:46.0
Silicone contamination is known to have a negative impact on assembly processes such as soldering, adhesive bonding, coating, and wire bonding. In particular, silicone is known to cause de-wetting of materials from surfaces and can result in adhesive failures. There are many sources for silicone contamination with common sources being mold releases or lubricants on manufacturing tools, offgassing during cure of silicone paste adhesives, and residue from pressure sensitive tape. This effort addresses silicone contamination by quantifying adhesive effects under known silicone contaminations. The first step in this effort identified an FT-IR spectroscopic detection limit for surface silicone utilizing the area under the 1263 cm-1 (Si-CH3) absorbance peak as a function of concentration (µg/cm2). The next step was to pre-contaminate surfaces with known concentrations of silicone oil and assess the effects on surface wetting and adhesion. This information will be used to establish guidelines for silicone contamination in different manufacturing areas within Harris Corporation... First published in the 2012 IPC APEX EXPO technical conference proceedings.
Career Center | , India | Engineering,Production,Quality Control,Research and Development,Sales/Marketing,Technical Support
I am working as lab chemist and also involved in troubleshooting and process control of various processes in pcb industry
ASYMTEK Products | Nordson Electronics Solutions | https://www.nordson.com/en/divisions/march/about-us/events/smta-amsterdam
Coating Performance" on Wednesday, May 24, 2017. For more information about the show visit: http://www.smta.org/contamination/ Contact Us If you experience any difficulties submitting your information, please email us. First Name * Last Name * Company * Email
| https://www.eptac.com/ask/maximum-limits-of-solder-bath-contamination/
Maximum Limits of Solder Bath Contamination - EPTAC - Train. Work Smarter. Succeed Looking for solder training standards, manuals, kits, and more
COT specializes in high quality SMT nozzles and consumables for pick and place machines. We provide special engineering design service of custom nozzles for those unique and odd components.
2481 Hilton Drive
Gainesville, GA USA
Phone: (770) 538-0411